Balloons made from liquid crystal polymer blends

Abstract

Balloons for use on medical devices such as catheter balloons are formed from polymer blend products which include a liquid crystal polymer (LCP), a crystallizable thermoplastic polymer, especially thermoplastic polyesters such as PET, and a compatabilizer. The compatabilizer may be an ethylene-maleic anhydride copolymer, an ethylene-methyl acrylate copolymer, an ethylene-methyl acrylate copolymer, an ethylene-methyl acrylate-maleic anhydride terpolymer, an ethylene-methyl-methacrylic acid terpolymer, an acrylic rubber, an ethylene-ethyl acrylate-glycidyl methacrylate terpolymer or a mixture of two or more such polymers.

1 . A balloon formed of an extruded tubular parison comprising one or more layers of polymeric material, by radial expansion under pressure at an elevated temperature below the lowest temperature which will melt a said layer, wherein the polymeric material of at least one said layer is a polymer melt blend product of 
 a) a thermotropic main-chain liquid crystal polymer (LCP);    b) a crystallizable thermoplastic polymer; and    c) at least one compatabilizer for a) and b).    
     
     
         2 . A balloon as in    claim 1    wherein said compatabilizer component c) includes a member selected from the group consisting of maleic acid grafted styreneethylene-butadiene-styrene block copolymers, alkyl (meth)acrylate-ethylene-glycidyl (meth)acrylate polymers; copolyester elastomers; ethylene unsaturated ester copolymers; copolymers of ethylene and a carboxylic acid or acid derivative; polyolefins or ethylene-unsaturated ester copolymers grafted with functional monomers; copolymers of ethylene and a carboxylic acid or acid derivative; terpolymers of ethylene, unsaturated ester and a carboxylic acid or acid derivative; ionomeric copolymers; and acrylic elastomers.  
     
     
         3 . A balloon as in    claim 1    wherein said compatabilizer component c) comprises at least one member selected from the group consisting of ethylene-maleic anhydride copolymers, ethylene-methyl acrylate copolymers, ethylene-methyl acrylate copolymers, ethylene-methyl acrylate-maleic anhydride terpolymers, ethylene-methyl-methacrylic acid terpolymers, acrylic rubbers and ethylene-ethyl acrylate-glycidyl methacrylate terpolymers.  
     
     
         4 . A balloon as in    claim 1    wherein the crystallizable thermoplastic polymer component b) is selected from polyesters, and polyamides.  
     
     
         5 . A balloon as in    claim 4    wherein the polyester is selected from the group consisting of alkylene phthalate polyesters, alkylene phthalate copolyesters, alkylene naphthalate polyesters, alkylene naphthalate copolyesters and alkylene phthalate/napthalate copolyesters.  
     
     
         6 . A balloon as in    claim 1    wherein the thermotropic main-chain liquid crystal polymer component a) is poly(oxybenzoyl-co-bisphenyl terephthalate) or poly (oxybenzoyl-co-oxynaphthoate).  
     
     
         7 . A balloon as in    claim 6    wherein the crystallizable thermoplastic polymer component b) is polyethylene terephthalate; and the compatabilizer component c) comprises at least one member selected from the group consisting of ethylene-maleic anhydride copolymers, ethylene-methyl acrylate copolymers, ethylene-methyl acrylate copolymers, ethylene-methyl acrylate-maleic anhydride terpolymers, ethylene-methyl-methacrylic acid terpolymers, acrylic rubbers and ethylene-ethyl acrylate-glycidyl methacrylate terpolymers.  
     
     
         8 . A balloon as in    claim 7    wherein the thermotropic main-chain liquid crystal polymer component a) is utilized in said polymer melt blend product in an amount of from about 0.1 to about 10 weight percent; the crystallizable thermoplastic polymer component b) is utilized in said polymer melt blend product in an amount of from about 40 to about 99 weight percent; and the compatabilizer component c) is utilized in said polymer melt blend product in an amount of from about 0.1 to about 30 weight percent.  
     
     
         9 . A balloon as in    claim 1    wherein the thermotropic main-chain liquid crystal polymer component a) is utilized in said polymer melt blend product in an amount of from about 0.1 to about 10 weight percent; the crystallizable thermoplastic polymer component b) is utilized in said polymer melt blend product in an amount of from about 40 to about 99 weight percent; and the compatabilizer component c) is utilized in said polymer melt blend product in an amount of from about 0.1 to about 30 weight percent.  
     
     
         10 . A balloon as in    claim 9    wherein the thermotropic main-chain liquid crystal polymer component a) is utilized in said polymer melt blend product in an amount of from about 0.5 to about 2 weight percent; the crystallizable thermoplastic polymer component b) is utilized in said polymer melt blend product in an amount of from about 85 to about 99 weight percent; and the compatabilizer component c) is utilized in said polymer melt blend product in an amount of from about 1 to about 10 weight percent.  
     
     
         11 . A catheter having an inflatable balloon according to    claim 1    mounted thereon.  
     
     
         12 . A catheter having an inflatable balloon according to    claim 9    mounted thereon.