Poly (vinyl alcohol) hydrogel

Abstract

The present invention comprises a poly (vinyl alcohol) hydrogel construct having a wide range of mechanical strengths for use as a human tissue replacement. The hydrogel construct may comprise a tissue scaffolding, a low bearing surface within a joint, or any other structure which is suitable for supporting the growth of tissue.

What is claimed is:  
     
         1 . A biocompatible construct consisting essentially of a PVA polymer and water, said construct having the following further properties: 
 a compressive modulus of elasticity between about 0.1 megaPascals and about 10 megaPascals, and    a glass transition temperature greater than about 40 degrees C.    
     
     
         2 . The biocompatible construct of    claim 1   , said construct having the following swelling properties: the material dimensions of said construct change less than 20% by swelling following hydration by submersion in an aqueous solution.  
     
     
         3 . The biocompatible construct of    claim 2    and further defined as having its hydrated dimensions reduced by less than 20% following submersion in an aqueous solution.  
     
     
         4 . A biocompatible hydrogel joint resurfacing agent comprising: 
 a semicrystalline organic polymer; and    water;    said joint resurfacing agent being further defined as having the following properties: a water content greater than about 20%, by weight; a coefficient of friction of less than 0.1; and a compressive modulus of elasticity of between about 0.1 megaPascals and about 10 megaPascals.    
     
     
         5 . The biocompatible hydrogel of    claim 4   , further defined as having a water content of between about 20% and about 95% by weight.  
     
     
         6 . A PVA construct consisting essentially of: 
 a PVA polymer; and    saline;    said construct having a compressive modulus of elasticity of between about 0.5 megaPascals and about 10 megaPascals and a glass transition temperature greater than 40° C., said construct being further defined as having been prepared according to the following steps:    pouring an aqueous PVA polymer mixture into a mold;    freezing and thawing said PVA polymer mixture within said mold at least once to create an interlocking mesh between PVA polymer molecules to create the semicrystalline organic hydrogel;    allowing for expansion of said PVA hydrogel within said mold.    
     
     
         7 . A biocompatible hydrogel joint resurfacing agent comprising: 
 a semi-crystalline organic polymer; and    a water content greater than about 20% by weight;    said hydrogel having a compressive modulus of elasticity of between about 0.5 megaPascals and about 10 megaPascals and a glass transition temperature greater than 40° C., said construct being further defined as having been prepared according to the following steps:    pouring an aqueous semi-crystalline organic polymer mixture into a mold;    freezing and thawing said semi-crystalline organic polymer mixture within said mold at least once to create an interlocking mesh between semi-crystalline organic polymer molecules to create the semi-crystalline organic polymer hydrogel;    allowing for expansion of said semi-crystalline organic polymer hydrogel, at least partially within said mold.    
     
     
         8 . The biocompatible hydrogel of    claim 7    which further contains eukaryotic cells.  
     
     
         9 . The PVA hydrogel of    claim 8   , wherein said eukaryotic cells are selected from the group consisting of: endothelial cells, aortic endothelial cells, smooth muscle cells, fibroblasts, dermal fibroblasts, and connective tissue cells.  
     
     
         10 . The biocompatible hydrogel of    claim 7    which further contains radioisotopes.