Abstract

The novel transparent polyolefin, polyester or polyamide article disclosed is stabilized against the effects of light, oxygen, heat and agressive chemicals by addition of 0.005-0.30% by weight the polymeric substrate of a hydroxyphenyl triazine UV absorber, and is characterized by its thickness between 1 and 500 μm. Preferred polyolefin articles thus stabilized are agricultural films containing as further stabilizer a sterically hindered amine. The novel compositions act as selective UV filter especially useful in agriculture.

1 . Transparent polyolefin, polyester or polyamide article having a thickness between 1 and 200 μm, which is stabilized against the effects of light, oxygen, heat and/or aggressive chemicals by addition of 0.005-0.30% by weight, based on the polyolefin, polyester or polyamide, of a hydroxyphenyl triazine UV absorber and containing a sterically hindered amine as further stabilizer.  
     
     
         2 . Transparent polyolefin article of  claim 1 .  
     
     
         3 . Transparent polyolefin, polyester or polyamide article of  claim 1  containing as further stabilizer a sterically hindered amine in an amount of 0.01-6% by weight the polyolefin, polyester or polyamide.  
     
     
         4 . Transparent polyolefin, polyester or polyamide article of  claim 3  wherein the weight ratio sterically hindered amine:hydroxyphenyl triazine UV absorber ranges from 2:1 to 20:1.  
     
     
         5 . Transparent polyolefin, polyester or polyamide article of  claim 3  wherein the sterically hindered amine belongs to the class of hydroxylamine ethers.  
     
     
         6 . Transparent polyolefin, polyester or polyamide article of  claim 1  wherein the hydroxyphenyl triazine UV absorber conforms to the formula I  
       
         
           
           
               
               
           
         
       
       wherein 
 R 1  is H or OR 7 ;  
 R 2  and R 3  independently are H, C 1 -C 8 alkyl,  
                     
  , OR 9 ;  
 R 4  and R 5  independently are H, C 1 -C 8 alkyl, OR 10 ;  
 R 6  is H, C 1 -C 18 alkyl, C 5 -C 12 cycloalkyl, C 7 -C 12 phenylalkyl, C 7 -C 12 alkylphenyl, C 3 -C 12 alkenyl, halogen, OH, OR 9 ;  
 R 8  is H; halogen; C 1 -C 12 alkoxy; C 1 -C 12 alkyl; C 3 -C 24 alkyl interrupted by oxygen and/or substituted by OH; or is NH—CO—R 14  or NH—COO—R 12 ;  
 R 7 , R 9  and R 10  independently are H; C 1 -C 24 alkyl; C 3 -C 12 alkenyl; C 3 -C 24 alkyl interrupted by oxygen and/or substituted by OH; or is C 5 -C 12 cycloalkyl, C 7 -C 12 phenylalkyl, C 7 -C 12 alkylphenyl;  
 CH 2 CH(OH)CH 2 OR 11 ; C 1 -C 12 alkyl substituted by COOR 12 , CONR 13 R 14 , OCOR 15 , OH or halogen; or R 7  is a polymeric hydrocarbon residue of 10 to 1000 carbon atoms;  
 and R 7  also embraces a residue of formula II  
                     
 wherein X is C 2 -C 24 alkylene; —CH 2 CH(OH)CH 2 —; —CH 2 CH(OH)CH 2 O-D-OCH 2 CH(OH)CH 2 ;  
 (C 1 -C 18 alkylene)-CO—O-D-O—CO—(C 1 -C 18 alkylene); CO; CO—(C 2 -C 24 alkylene)-CO;  
 C 3 -C 24 alkylene interrupted by oxygen;  
 D is C 2 -C 12 alkylene; C 4 -C 50 alkylene interrupted by O; phenylene; biphenylene or phenylene-E-phenylene;  
 E is O, S, SO 2 ; CH 2 ; CO or —C(CH 3 ) 2 —;  
 R 11  is H, C 1 -C 12 alkyl; phenyl; phenyl substituted by 1-3 C 1 -C 4 alkyl; C 5 -C 12 cycloalkyl; C 7 -C 12 phenylalkyl;  
 C 3 -C 12 alkenyl;  
 R 12  is H; C 1 -C 24 alkyl; C 3 -C 12 alkenyl; C 3 -C 36 alkyl interrupted by oxygen and/or substituted by OH; or is C 5 -C 12 cycloalkyl, C 7 -C 12 phenylalkyl, C 7 -C 12 alkylphenyl; phenyl;  
 R 13  and R 14  independently are H, C 1 -C 18 alkyl; phenyl; phenyl substituted by 1-3 C 1 -C 4 alkyl and/or C 1 -C 4 alkoxy; C 5 -C 12 cycloalkyl; C 3 -C 12 alkenyl;  
 R 15  is C 1 -C 12 alkyl; phenyl; phenyl substituted by 1-3 C 1 -C 4 alkyl and/or C 1 -C 4 alkoxy; C 5 -C 12 cycloalkyl;  
 C 3 -C 12 alkenyl; C 1 -C 12 alkoxy; or is NR 13 R 14 .  
 
     
     
         7 . Transparent polyolefin, polyester or polyamide article of  claim 6 , wherein in the hydroxyphenyl triazine UV absorber of formula I 
 R 2  and R 3  independently are H, methyl,                           , OR 9 ;    R 4  and R 5  independently are H or methyl;    R 6  is H;    R 8  is H; C 1 -C 8 alkoxy; C 1 -C 8 alkyl;    R 7 , R 9  independently are H; C 1 -C 18 alkyl; C 3 -C 12 alkenyl; C 3 -C 24 alkyl interrupted by oxygen and/or substituted by OH; or is C 5 -C 12 cycloalkyl, C 7 -C 12 phenylalkyl, C 7 -C 12 alkylphenyl; C 1 -C 12 alkyl substituted by COOR 12 , OCOR 15 , OH; or R 7  is a polymeric hydrocarbon residue of 20 to 500 carbon atoms;    and R 7  also embraces a residue of formula II, wherein X is C 2 -C 18 alkylene; —CH 2 CH(OH)CH 2 —; —CH 2 CH(OH)CH 2 O-D-OCH 2 CH(OH)CH 2 ;    (C 1 -C 4 alkylene)-CO—O-D-O—CO—(C 1 -C 4 alkylene); CO; CO—(C 2 -C 18 alkylene)-CO;    C 3 -C 18 alkylene interrupted by oxygen; D is C 2 -C 12 alkylene;    R 12  is H; C 1 -C 24 alkyl; C 3 -C 12 alkenyl; C 3 -C 24 alkyl interrupted by oxygen and/or substituted by OH; or is C 5 -C 12 cycloalkyl, C 7 -C 12 phenylalkyl, C 7 -C 12 alkylphenyl; phenyl;    R 15  is C 1 -C 12 alkyl; C 5 -C 12 cycloalkyl; C 3 -C 12 alkenyl.    
     
     
         8 . Transparent polyolefin, polyester or polyamide article of  claim 1  which is a film, fiber, ribbon or stretched tape.  
     
     
         9 . Transparent polyolefin, polyester or polyamide article of  claim 8  which is a polyolefin agricultural film.  
     
     
         10 . Transparent polyolefin article of  claim 1 , wherein the polyolefin is polyethylene or polypropylene.  
     
     
         11 . Transparent polyolefin, polyester or polyamide article of  claim 1  additionally containing a further component selected from the group consisting of processing stabilizers, fillers, clarifiers, modifiers, acid scavengers, flame retardants and, further light stabilizers.  
     
     
         12 - 16 . (cancelled).  
     
     
         17 . Transparent polyolefin, polyester or polyamide article of  claim 1  wherein the sterically hindered amine is selected from 
 bis(2,2,6,6-tetramethyl-4-piperidyl)sebacate,    bis(2,2,6,6-tetramethyl-4-piperidyl)succinate,    bis(1,2,2,6,6-pentamethyl-4-piperidyl)sebacate,    bis(1,2,2,6,6-pentamethyl-4-piperidyl) n-butyl-3,5-di-tert-butyl-4-hydroxybenzylmalonate,    the condensate of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid,    linear or cyclic condensates of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)-hexamethylenediamine and 4-tert-octylamino-2,6-dichloro-1,3,5-triazine,    tris(2,2,6,6-tetramethyl-4-piperidyl)nitrilotriacetate,    tetrakis(2,2,6,6-tetramethyl-4-piperidyl)-1,2,3,4-butanetetracarboxylate,    1,1′-(1,2-ethanediyl)-bis(3,3,5,5-tetramethylpiperazinone),    4-benzoyl-2,2,6,6-tetramethylpiperidine,    4-stearyloxy-2,2,6,6-tetramethylpiperidine,    bis(1,2,2,6,6-pentamethylpiperidyl)-2-n-butyl-2-(2-hydroxy-3,5-di-tert-butylbenzyl)malonate,    3-n-octyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4-dione,    linear or cyclic condensates of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-morpholino-2,6-dichloro-1,3,5-triazine,    the condensate of 2-chloro-4,6-bis(4-n-butylamino-2,2,6,6-tetramethylpiperidyl)-1,3,5-triazine and 1,2-bis(3-aminopropylamino)ethane,    the condensate of 2-chloro-4,6-di-(4-n-butylamino-1,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazine and 1,2-bis(3-aminopropylamino)ethane,    8-acetyl-3-dodecyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4-dione,    3-dodecyl-1-(2,2,6,6-tetramethyl-4-piperidyl)pyrrolidine-2,5-dione,    3-dodecyl-1-(1,2,2,6,6-pentamethyl-4-piperidyl)pyrrolidine-2,5-dione,    a mixture of 4-hexadecyloxy- and 4-stearyloxy-2,2,6,6-tetramethylpiperidine,    a condensate of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-cyclohexylamino-2,6-dichloro-1,3,5-triazine,    a condensate of 1,2-bis(3-aminopropylamino)ethane and 2,4,6-trichloro-1,3,5-triazine as well as 4-butylamino-2,2,6,6-tetramethylpiperidine;    a condensate of 1,6-hexanediamine and 2,4,6-trichloro-1,3,5-triazine as well as N,N-dibutylamine and 4-butylamino-2,2,6,6-tetramethylpiperidine;    N-(2,2,6,6-tetramethyl-4-piperidyl)-n-dodecylsuccinimide,    N-(1,2,2,6,6-pentamethyl-4-piperidyl)-n-dodecylsuccinimide,    2-undecyl-7,7,9,9-tetramethyl-1-oxa-3,8-diaza-4-oxo-spiro[4,5]decane,    a reaction product of 7,7,9,9-tetramethyl-2-cycloundecyl-1-oxa-3,8-diaza-4-oxospiro-[4,5]decane and epichlorohydrin,    1,1-bis(1,2,2,6,6-pentamethyl-4-piperidyloxycarbonyl)-2-(4-methoxyphenyl)ethene,    N,N′-bis-formyl-N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine,    a diester of 4-methoxymethylenemalonic acid with 1,2,2,6,6-pentamethyl-4-hydroxypiperidine,    poly[methylpropyl-3-oxy-4-(2,2,6,6-tetramethyl-4-piperidyl)]siloxane,    a reaction product of maleic acid anhydride-α-olefin copolymer with 2,2,6,6-tetramethyl-4-aminopiperidine or 1,2,2,6,6-pentamethyl-4-aminopiperidine;    N,N′,N″,N′″-Tetrakis(4,6-bis(butyl-(N-methyl-2,2,6,6-tetramethylpiperidin-4-yl)amino)triazin-2-yl)-4,7-diazadecane-1,10-diamine;                          where n is from the range 3-5;    sterically hindered hydroxylamine ethers, and mixtures of these compounds;    and contained in an amount of 0.01 to 6% by weight of the polyolefin, polyester or polyamide.