Black iron-based particles and black toner containing the same

Abstract

Black iron-based particles comprise a FeTiO 3 —Fe 2 O 3 solid solution or a mixed composition of a FeTiO 3 —Fe 2 O 3 solid solution and an iron-based oxide having a spinel structure, and having a Ti content of from more than 10.0 atm % to 40.0 atm %, calculated as Ti, based on whole Fe, and a blackness (L* value) of 6 to 13.

1 . Black iron-based particles comprising a FeTiO 3 —Fe 2 O 3  solid solution or a mixed composition of a FeTiO 3 —Fe 2 O 3  solid solution and an iron-based oxide having a spinel structure, and having a Ti content of from more than 10.0 atm % to 40.0 atm %, calculated as Ti, based on whole Fe, and a blackness (L* value) of 6 to 13.  
     
     
         2 . Black iron-based particles according to  claim 1 , wherein said iron-based oxide having a spinel structure is contained in such an amount that a ratio of a peak intensity of (220) plane of Fe 3 O 4 -γ-Fe 2 O 3  constituting the iron-based oxide having a spinel structure to a peak intensity of (104) plane of FeTiO 3 —Fe 2 O 3  is 1:0.5 or less, when measured by an X-ray diffraction method.  
     
     
         3 . Black iron-based particles according to  claim 2 , wherein said ratio of a peak intensity of (220) plane of Fe 3 O 4 -γ-Fe 2 O 3  constituting the iron-based oxide having a spinel structure to a peak intensity of (104) plane of FeTiO 3 —Fe 2 O 3  is 1:0.01 to 1:0.45.  
     
     
         4 . Black iron-based particles according to  claim 1 , wherein said black iron-based particles have a saturation magnetization value of not more than 60 Am 2 /kg and an average particle diameter of 0.01 to 0.50 μm.  
     
     
         5 . Black iron-based particles according to  claim 1 , wherein said black iron-based particles have a Ti content of 20 to 33.3 atm %, calculated as Ti, based on whole Fe, a saturation magnetization value of 0.1 to 40 Am 2 /kg, a blackness (L* value) of 6 to 12.5 and an average particle diameter of 0.04 to 0.24 μm.  
     
     
         6 . Black iron-based particles according to  claim 1 , wherein said black iron-based particles have a BET specific surface area value of 6 to 30 m 2 /g and a tinting strength of 35 to 45.  
     
     
         7 . Black iron-based particles according to  claim 1 , which further comprise a Na—Fe—Ti compound.  
     
     
         8 . Black iron-based particles according to  claim 7 , wherein said Na—Fe—Ti compound is contained in such an amount that a ratio of a main peak intensity of the Na—Fe—Ti compound to a peak intensity of (104) plane of FeTiO 3 —Fe 2 O 3  is 0.01:1 to 1.00:1, when measured by an X-ray diffraction method.  
     
     
         9 . Black iron-based particles according to  claim 7 , wherein said Na—Fe—Ti compound is NaFeTi 3 O 8 , NaFeTiO 4  or Na 0.75 Fe 0.75 Ti 0.25 O 2 .  
     
     
         10 . Black iron-based particles according to  claim 7 , wherein said black iron-based particles have a saturation magnetization value of 0.1 to 60 Am 2 /kg.  
     
     
         11 . Black iron-based particles according to  claim 1 , which further comprise a blue pigment in an amount of 0.1 to 20% by weight.  
     
     
         12 . Black iron-based particles according to  claim 11 , wherein said black iron-based particles have a blackness (L* value) of 6 to 12 and a tinting strength of 30 to 42.  
     
     
         13 . Black iron-based particles a FeTiO 3 —Fe 2 O 3  solid solution or a mixed composition of a FeTiO 3 —Fe 2 O 3  solid solution and an iron-based oxide having a spinel structure, and having a Ti content of from more than 10.0 atm % to 40.0 atm %, calculated as Ti, based on whole Fe, a blackness (L* value) of 6 to 13, a saturation magnetization value of 5 to 40 Am 2 /kg and an average particle diameter of 0.04 to 0.24 Am.  
     
     
         14 . Black iron-based particles comprising: 
 a FeTiO 3 —Fe 2 O 3  solid solution or a mixed composition of a FeTiO 3 —Fe 2 O 3  solid solution and an iron-based oxide having a spinel structure, and a Na—Fe—Ti compound,    and having a Ti content of from more than 10.0 atm % to 40.0 atm %, calculated as Ti, based on whole Fe, a saturation magnetization value of 0.1 to 60 Am 2 /kg, a blackness (L* value) of 6 to 13 and an average particle diameter of 0.04 to 0.24 μm, said Na—Fe—Ti compound being contained in such an amount that a ratio of a main peak intensity of the Na—Fe—Ti compound to a peak intensity of (104) plane of FeTiO 3 —Fe 2 O 3  is 0.01:1 to 1.00:1, when measured by an X-ray diffraction method.    
     
     
         15 . Black iron-based particles comprising: 
 (1) 80 to 99.9 parts by weight of a FeTiO 3 —Fe 2 O 3  solid solution or a mixed composition of a FeTiO 3 —Fe 2 O 3  solid solution and an iron-based oxide having a spinel structure; and (2) 0.1 to 20 parts by weight of a blue pigment,    and having a Ti content of from more than 10.0 atm % to 40.0 atm %, calculated as Ti, based on whole Fe, a saturation magnetization value of 5 to 40 Am 2 /kg, a blackness (L* value) of 6 to 13 and an average particle diameter of 0.04 to 0.24 μm.    
     
     
         16 . Black iron-based particles according to  claim 13 , wherein said iron-based oxide having a spinel structure is contained in such an amount that a ratio of a peak intensity of (220) plane of Fe 3 O 4 -γ-Fe 2 O 3  constituting the iron-based oxide having a spinel structure to a peak intensity of (104) plane of FeTiO 3 —Fe 2 O 3  is 1:0.5 or less, when measured by an X-ray diffraction method.  
     
     
         17 . A black non-magnetic toner comprising a binder resin and the black iron-based particles as defined in  claim 1.