Process for producing aryl-aryl coupled compounds

Abstract

The invention relates to the preparation of aryl-aryl coupled compounds and materials. These materials play an important role in industry, for example as liquid crystals, pharmaceuticals and agrochemicals, to mention just a few application areas. These compounds, in particular, are also of major importance especially in the high-growth area of organic semi-conductors (for example, applications in organic or polymeric light-emitting diodes, organic solar cells, organic ICs).

1 . (canceled)  
     
     
         2 . A poly-arylene or -heteroarylene as claimed in  claim 19 , characterised in that the aryl or heteroaryl compounds and the aromatic or heteroaromatic radicals of the corresponding boron compounds denote aromatic or heteroaromatic entities containing from 2 to 40 c atoms which may be substituted by one or more linear, branched or cyclic alkyl or alkoxy radicals containing from 1 to 20 c atoms wherein one or more non-consecutive CH 2  groups may also have been replaced by O, S, C═O or a carboxy group, substituted or unsubstituted C-2 to C-20 aryl or heteroaryl radicals, fluorine, cyano, nitro or sulphonic acid derivatives, or which may be unsubstituted.  
     
     
         3 . Poly-arylene or -heteroarylene according to  claim 2  wherein said halogen- or sulphonyloxy-functionalized aryl or heteroaryl are compounds of formula (I)  
         Ar—(X) n   (I)  
       wherein 
 Ar is an aryl or heteroaryl radical as defined in  claim 2 ,  
 X denotes —Cl, —Br, —I, —OS(O) 2 R 1 ,  
 and R 1  is an alkyl, aryl or fluorinated alkyl radical,  
 and n denotes at least 1.  
 
     
     
         4 . Poly-arylene or -heteroarylene according to  claim 2 , wherein the aromatic or heteroaromatic boron compounds are of the general formula (II)  
         Ar—(BQ 1 Q 2 ) m   (II)  
       wherein 
 Ar is an aryl or heteroaryl radical as defined in  claim 2 ,  
 Q 1  and Q 2  are the same or different and denote —OH, C 1 -C 4 alkoxy, C 1 -C 4 aryloxy,  
 C 1 -C 4 alkyl or halogen, or Q 1  and Q 2  together form a C 1 -C 4 alkylenedioxy group which may optionally be substituted by one or more C 1 -C 4 alkyl groups, or Q 1  and Q 2  and the boron atom together are part of a boroxine ring of formula (III)  
                     
 and m denotes at least 1.  
 
     
     
         5 . Poly-arylene or -heteroarylene according to  claim 19 , wherein the palladium compound consists of a palladium source and optionally one or more additional components, 
 the palladium source being either salts of palladium(II), or palladium(0) compounds or complexes or also metallic palladium,    and the additional components being ligands which can coordinate at the palladium metal centre.    
     
     
         6 . Poly-arylene or -heteroarylene according to  claim 5 , wherein said additional component(s)are phosphine ligands from the group of tri-aryl-phosphines, di-aryl-alkyl-phosphines, aryl-dialkyl-phosphines, trialkyl-phosphines, tri-heteroaryl-phosphines, di-heteroaryl-alkyl-phosphines, heteroaryl-dialkyl-phosphines, optionally the substituents on the phosphorus to be the same or different, chiral or achiral, and optionally one or more of the substituents to link the phosphorus groups of a plurality of phosphines and optionally for some of those links to be one or more metal atoms, except that triphenylphosphine is not used.  
     
     
         7 . Poly-arylene or -heteroarylene according to  claim 19 , wherein said water-miscible organic solvents has at least one solvent which forms a clear, single-phase solution at room temperature both when at least 5% by weight water is present in the solvent and when at least 5% by weight solvent is present in water.  
     
     
         8 . Poly-arylene or -heteroarylene according to  claim 19 , wherein said water-immiscible organic solvent there is used at least one solvent which no longer forms a clear, single-phase solution at room temperature, that is to say phase separation is already discernible, even when less than 5% by weight water is present in the solvent or even when less than 5% by weight solvent is present in water.  
     
     
         9 . Poly-arylene or -heteroarylene according to  claim 19 , wherein in the process, a reaction of one multifunctional compound with a plurality of mono functional compounds to form one defined compound of low molecular weight is carried out.  
     
     
         10 . Poly-arylene or -heteroarylene according to  claim 19 , wherein in the process, at least two different multifunctional compounds are brought into reaction with one another and a polymeric product is obtained.  
     
     
         11 . Poly-arylene or -heteroarylene according to  claim 10 , characterised in that the polymerisation is carried out in at least two steps, an excess of one monomer being employed in the first step so that a short-chain polymer having a first composition is formed, and the remaining monomers being subsequently added in one or more further step(s) so that finally the ratio of boron-containing reactive groups and halogen- or sulphonyloxy-containing reactive groups is 1:1.  
     
     
         12 . Poly-arylene or -heteroarylene according to  claim 11 , characterised in that the monomer composition of the second or further steps is different to that of the first step, as a result of which polymers having a block structure are formed.  
     
     
         13 . Poly-arylene or -heteroarylene, having a weight-average degree of polymerisation DP 2  of at least 1000.  
     
     
         14 . (canceled)  
     
     
         15 . Electronic components comprising one or more polymer(s) according to  claim 13 .  
     
     
         16 . Poly-arylene or -heteroarylene according to  claim 3 , wherein n is 1 to 20.  
     
     
         17 . Poly-arylene or -heteroarylene according to  claim 4 , wherein m is 1 to 20.  
     
     
         18 . Poly-arylene or -heteroarylene according to  claim 13  having a M n  in the range of 150,000 to 410,000 g/mol.  
     
     
         19 . A poly-arylene or -heteroarylene having a weight-average degree of polymerisation DP w  of at least 1000 obtained by the process of reacting a halogen- or sulphonyloxy-functional aryl or heteroaryl compound with an aromatic or heteroaromatic boron compound in the presence of a catalytic amount of a palladium compound, a base and a multi-phase solvent mixture wherein an aryl-aryl or aryl-heteroaryl or heteroaryl-heteroaryl C—C bond is formed, characterised in that 
 a. the solvent mixture comprises at least 0.1% by volume of a compound from each of the following groups 
 i) water-miscible organic solvents  
 ii) water-immiscible organic solvents  
 iii) water,  
   with the proviso that both alcohols and carbonyl compounds which contain α-hydrogen atoms are excluded;    b. and the palladium compound does not contain triphenylphosphine or the latter is not specifically added to the reaction mixture.