Building exterior wall-coating emulsion compositions and building exterior walls

Abstract

An emulsion composition for building exterior walls is provided comprising in admixture, [A] a graft copolymerized emulsion obtained by adding to (1) an oil-in-water type emulsion containing at least one organopolysiloxane having an organic group containing a radical reactive group or SH group, (2) a monomer or monomeric mixture containing at least 70 wt % of at least one monomer selected from acrylic and methacrylic monomers and effecting emulsion graft polymerization of component (2) to the organopolysiloxane, and [B] a silicone resin-containing emulsion. The emulsion composition is capable of forming an elastic, flexible coating which is endowed with water resistance, weather resistance, water repellency, adhesion and heat resistance and maintains these properties over a long period of time. It can thus be used as a base in a variety of paints and coating agents.

1 . An emulsion composition for building exterior walls, comprising in admixture, 
 [A] a graft copolymerized emulsion obtained by adding to (1) an oil-in-water type emulsion containing at least one organopolysiloxane having the general formula (I):                          wherein R 1 , R 2  and R 3  each are a monovalent hydrocarbon group or monovalent halogenated hydrocarbon group having 1 to 20 carbon atoms, Y is an organic group containing a radical reactive group or SH group, X is hydrogen, a monovalent lower alkyl group or a group of the formula: R 1 R 2 R 4 Si wherein R 4  is R 1  or Y, and R 1 , R 2  and Y are as defined above, m is an integer of 1 to 10,000, and n is an integer of at least 1, (2) a monomer or monomeric mixture containing at least 70% by weight of at least one monomer selected from acrylic and methacrylic monomers having the general formula (II):                          wherein R 5  is hydrogen or methyl, and R 6  is an alkyl or alkoxy-substituted alkyl group having 1 to 18 carbon atoms, so that a weight ratio of the organopolysiloxane of component (1) and the monomer or monomeric mixture of component (2) is 5:95 to 95:5, and effecting emulsion graft polymerization of component (2) to the organopolysiloxane, and    [B] a silicone resin-containing emulsion obtained by mixing a silicone resin having the average compositional formula (i):      R 7   a R 8   b Si(OH) p (OX) q O (4−a−b−p−q)/2    (i)    wherein R 7  is an unsubstituted monovalent hydrocarbon group of 1 to 10 carbon atoms, R 8  is a substituted monovalent hydrocarbon group of 1 to 10 carbon atoms, X is a monovalent hydrocarbon group of 1 to 6 carbon atoms, a, b, p and q are positive numbers satisfying the range: 0.50≦a≦1.80, 0≦b≦1.00, 0<p≦1.50, 0≦q≦0.50, 0.50≦a+b≦1.80, 0<p+q≦1.50, and 0.50<a+b+p+q≦2.0, with a radical polymerizable vinyl monomer and effecting emulsion polymerization.    
     
     
         2 . The emulsion composition of  claim 1  wherein component (2) is a monomeric mixture of 
 (a) 70 to 98% by weight of at least one monomer selected from acrylic and methacrylic monomers having the general formula (II):                          wherein R 5  is hydrogen or methyl, and R 6  is an alkyl or alkoxy-substituted alkyl group having 1 to 18 carbon atoms,    (b) 2 to 10% by weight of at least one functional monomer selected from the group consisting of an ethylenically unsaturated amide, an alkylol or alkoxyalkyl-substituted compound of ethylenically unsaturated amide, an ethylenically unsaturated monomer containing an oxirane group, hydroxyl group, carboxyl group, amino group, sulfonate group, phosphate group, polyalkylene oxide group or quaternary ammonium base, a complete ester of a polyhydric alcohol with acrylic or methacrylic acid, allyl acrylate, allyl methacrylate and divinylbenzene, and    (c) 0 to 20% by weight of an ethylenically unsaturated monomer other than components (a) and (b).    
     
     
         3 . The emulsion composition of  claim 1  wherein a polymeric product of the monomer or monomeric mixture as component (2) has a glass transition temperature of up to 0° C.  
     
     
         4 . The emulsion composition of  claim 1 , further comprising a liquid organopolysiloxane containing at least three silicon-bonded hydrogen atoms in a molecule as a crosslinker and a catalyst for crosslinking reaction.  
     
     
         5 . A building exterior wall coated with the emulsion composition of  claim 1.