Gloss-coated paper with enhanced runnability and print quality

Abstract

This invention provides a gloss-coated electrophotographic paper with superior runnability and print quality in colour and monochrome copiers and printers. The coated paper product comprises a paper substrate coated on at least one side with a pigmented coating. The pigment coating consists of a mixture of at least three different pigments and a binder. The coating may further include a lubricant. Optionally, the coating formulation may contain an optical brightening agent, a defoamer and a thickener. In addition, the gloss coated electrophotographic paper of this invention provides a superior toner adhesion in colour and monochrome electrophotographic imaging applications.

1 - 28 . (canceled)  
   
   
       29 . A coated paper, comprising a paper substrate coated on at least one side with a pigmented coating having a Parker Print Surface of from 0.8 to 2.0; wherein said pigmented coating comprises a lubricant, a binder and at least three different pigments.  
   
   
       30 . The coated paper according to  claim 29 , wherein at least five different pigments are present in said pigmented coating.  
   
   
       31 . The coated paper according to  claim 29 , wherein at least six different pigments are present in said pigmented coating.  
   
   
       32 . The coated paper according to  claim 29 , wherein said pigments are selected from the group consisting of calcium carbonates, clay, plastic pigments, titanium oxide, calcined clay, satin white, silica, alumina silicates, talc, aluminium trihydrates and polymethyl methacrylate beads.  
   
   
       33 . The coated paper according to  claim 29 , wherein said pigments are selected from the group consisting of calcium carbonates, clay, plastic pigments, titanium oxide and calcined clay, all having particle sizes in the range of 0.1 to 2 microns.  
   
   
       34 . The coated paper according to  claim 29 , wherein said binder is selected from the group consisting of vinyl acetate acrylate, styrene acrylate and styrene butadiene acrylic copolymers.  
   
   
       35 . The coated paper according to  claim 29 , wherein said binder has a glass transition temperature in the range of from −5 to 30° C.  
   
   
       36 . The coated paper according to  claim 29 , wherein the Scott internal bond of the coated paper is in the range of from 150 to 500.  
   
   
       37 . The coated paper according to  claim 29 , wherein the delta coefficient of friction of the coated paper is in the range of from 0.06 to 0.20.  
   
   
       38 . The coated paper according to  claim 29 , wherein said paper substrate has a formation index greater than 70.  
   
   
       39 . The coated paper according to  claim 29 , wherein said paper substrate has a surface resistivity in the range from 1×10 10  ohms/square to 1×10 10  ohms/square.  
   
   
       40 . The coated paper according to  claim 29 , wherein the total amount of pigments in the coating is from 50 to 90 weight % and the amount of binder in the coating is from 8 to 20 weight % based on the total weight of the coating.  
   
   
       41 . The coated paper according to  claim 29 , wherein said pigments in said pigmented coating comprise calcium carbonate present from 25 to 75 weight %; clay present from 20 to 70 weight %; calcined clay present from 2 to 10 weight %; and plastic pigment present from 2 to 10 weight %, wherein the weight %'s are based on the dry weight of the total pigment.  
   
   
       42 . The coated paper according to  claim 29 , wherein said pigmented coating is coated on both sides of said substrate.  
   
   
       43 . The coated paper according to  claim 29 , wherein said binder is selected from the group consisting of vinyl acetate, styrene acrylate and styrene butadiene acrylic copolymers and is present in amounts of 8 to 20 weight % based on the total weight of the coating.  
   
   
       44 . The coated paper according to  claim 29 , wherein the coated paper has a TAPPI 75-degree gloss ranging from 45 to 85%.  
   
   
       45 . The coated paper according to  claim 29 , wherein the coated paper has a TAPPI 75-degree gloss ranging from 68 to 85%.  
   
   
       46 . The coated paper according to  claim 29 , wherein at least four different pigments are present in said pigmented coating.  
   
   
       46 . The coated paper according to  claim 29 , wherein at least four different pigments are present in said pigmented coating.  
   
   
       47 . A method of making the coated paper according to  claim 29 , comprising contacting a paper substrate with a lubricant, a binder and at least three different pigments.  
   
   
       48 . A method of making the coated paper according to  claim 29 , comprising 
 contacting a paper substrate with a coating composition comprising a lubricant, a binder and at least three different pigments wherein the lubricant, a binder and at least three different pigments.