Process for the production of multi-layer coatings

Abstract

A process for the production of multi-layer coatings comprising the successive steps: 1) applying an 8 to 20 μm thick coating layer from an aqueous coating composition A onto a substrate provided with an EDC primer, 2) applying a 5 to 15 μm thick base coat layer from an aqueous coating composition B onto the previously applied coating layer, 3) applying a clear coat layer onto the base coat layer, 4) jointly curing the three coating layers, wherein coating compositions A and B being different from each other and wherein the coating composition A contains at least one metal platelet pigment having a thickness from 10 to 100 nm in a proportion corresponding to a pigment/resin solids ratio by weight from 0.06:1 to 0.2:1.

1 . A process for the production of multi-layer coatings comprising the successive steps: 
 (a) applying an 8 to 20 μm thick coating layer from an aqueous coating composition A onto a substrate provided with an EDC primer,    (b) applying a 5 to 15 μm thick base coat layer from an aqueous coating composition B onto the previously applied coating layer,    (c) applying a clear coat layer onto the base coat layer,    (d) jointly curing the three coating layers,    wherein coating compositions A and B being different from each other and    wherein the coating composition A contains at least one metal platelet pigment having a thickness from 10 to 100 nm in a proportion corresponding to a pigment/resin solids ratio by weight from 0.06:1 to 0.2:1.    
   
   
       2 . The process of  claim 1 , wherein the sum of the coating thickness for the two-layer coatings produced from the coating compositions A and B is 15 to 35 μm.  
   
   
       3 . The process of  claim 1  or  2 , wherein the resin solids of coating composition A comprise polyurethane resin and/or are crosslinkable by formation of urethane groups.  
   
   
       4 . The process of  claim 1  wherein the coating composition B is distinguished in that UV light corresponding to a UV transmission of more than 0.1% in the wavelength range of from 280 to 380 nm and/or of more than 0.5% in the wavelength range of from 380 to 400 nm and/or of more than 1% in the wavelength range of from 400 to 450 nm may penetrate through a two-layer coating structure consisting of a 10 μm thick layer applied from a mixture produced in a resin solids ratio by weight of 1.5 pbw coating composition B to 1 pbw trimeric hexane diisocyanate-polyisocyanate, and a 5 μm thick layer applied from the coating composition B itself.  
   
   
       5 . The process of  claim 1  wherein the substrate provided with an EDC primer is selected from the group consisting of automotive bodies and automotive body parts.  
   
   
       6 . Substrate coated with a multi-layer coating produced according to the process of any one of the preceding claims.