High heat polyethersulfone compositions

Abstract

High heat polyethersulfone compositions are provided which possess unexpectedly high glass transition temperatures. The polyethersulfone compositions comprise structural units derived from fluorenone bisphenols such as 9,9-bis(4-hydroxyphenyl)fluorene, and structural units derived from at least one biphenyl-bissulfone such as 4,4′-bis((4-chlorophenyl)sulfonyl)-1,1′-biphenyl. The novel polyethersulfone compositions may further comprise structural units derived from one or more biphenols such as 4,4′-biphenol, bisphenols such as BPA, or other electrophilic sulfone monomers, such as bis(4-chlorophenyl)sulfone. In one embodiment, the polyethersulfone composition of the present invention comprises structural groups derived exclusively from 9,9-bis(4-hydroxyphenyl)fluorene and 4,4′-bis((4-chlorophenyl)sulfonyl)-1,1′-biphenyl and exhibits a single glass transition of greater than 300° C.

1 . A polyethersulfone composition comprising structural units I  
       
         
           
           
               
               
           
         
       
       wherein R 1 , R 2 , R 3 , and R 4  are independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “a”, “b”, “c”, “d”, “e”, “f”, “g” and “h” are independently integers from 0 to 4.  
     
     
         2 . The polyethersulfone composition according to  claim 1 , said composition having a glass transition temperature of at least 270° C.  
     
     
         3 . The polyethersulfone composition according to  claim 1 , said composition having a glass transition temperature of at least 250° C.  
     
     
         4 . The polyethersulfone composition according to  claim 1 , further comprising structural units II  
       
         
           
           
               
               
           
         
       
       wherein R 5  and R 6  are independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “i”, “j”, “k”, and “l” are independently integers from 0 to 4.  
     
     
         5 . The polyethersulfone composition according to  claim 1 , further comprising structural units II  
       
         
           
           
               
               
           
         
       
       wherein R 3 , R 4 , and R 5  are independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “e”, “f”, “g”, “h”, “i”, and “j” are independently integers from 0 to 4.  
     
     
         6 . The polyethersulfone composition according to  claim 1 , further comprising structural units IV  
       
         
           
           
               
               
           
         
       
       wherein R 1 , R 2 , and R 6  are independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “a”, “b”, “c”, “d”, “k”, and “l” are independently integers from 0 to 4.  
     
     
         7 . The polyethersulfone composition according to  claim 1 , wherein “a”, “b”, “c”, “d”, “e”, “f”, “g” and “h” are each zero.  
     
     
         8 . The polyethersulfone composition according to  claim 4 , wherein “i”, “j”, “k”, and “l” are each zero.  
     
     
         9 . The polyethersulfone composition according to  claim 5 , wherein “e”, “f”, “g”, “h”, “i”, and “j” are each zero.  
     
     
         10 . The polyethersulfone composition according to  claim 6 , wherein “a”, “b”, “c”, “d”, “k”, and “l” are each zero.  
     
     
         11 . The polyethersulfone composition according to  claim 1 , further comprising structural units derived from at least one bisphenol V  
       
         
           
           
               
               
           
         
       
       wherein R 7  is independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; W an oxygen atom, a sulfur atom, a selenium atom, a divalent C 1 -C 20  aliphatic radical, a divalent C 3 -C 20  cycloaliphatic radical, or a divalent C 2 -C 20  aromatic radical; and “m”, and “n” are independently integers from 0 to 4.  
     
     
         12 . The polyethersulfone composition according to  claim 1 , further comprising structural units derived from bisphenol A.  
     
     
         13 . A polyethersulfone composition comprising structural units derived from at least one fluorenone bisphenol VI  
       
         
           
           
               
               
           
         
       
       wherein R 1  and R 2  are independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “a”, “b”, “c”, and “d” are independently integers from 0 to 4;  
       at least one biphenyl-bissulfone VII  
       
         
           
           
               
               
           
         
       
       wherein X 1  and X 2  are independently halogen, or nitro; R 3  and R 4  are independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “e”, “f”, “g”, and “h” are independently integers from 0 to 4; and  
       optionally structural units derived from at least one biphenol VIII  
       
         
           
           
               
               
           
         
       
       wherein R 5  is independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “i” and “j” are independently integers from 0 to 4.  
     
     
         14 . The polyether sulfone composition according to  claim 13 , wherein the structural units derived from fluorenone bisphenol VI represent from about 10 mole percent to about 100 mole percent of all structural groups derived from a dihydroxy aromatic compound present in the composition.  
     
     
         15 . The polyether sulfone composition according to  claim 13 , wherein the structural units derived from biphenol VIII represent from about 0 mole percent to about 90 mole percent of all structural groups derived from a dihydroxy aromatic compound present in the composition.  
     
     
         16 . The polyethersulfone composition according to  claim 13 , further comprising structural units derived from at least one sulfone IX  
       
         
           
           
               
               
           
         
       
       wherein X 3  and X 4  are independently halogen, or nitro; R 6  is independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “k” and “l” are independently integers from 0 to 4.  
     
     
         17 . The polyethersulfone composition according to  claim 16 , wherein the structural units derived from biphenyl-bissulfone VII represent from about 10 mole percent to about 70 mole percent of all structural groups derived from an electrophilic sulfone monomer.  
     
     
         18 . The polyethersulfone composition according to  claim 16 , wherein the structural units derived from sulfone IX represent from about 5 mole percent to about 50 mole percent of all structural groups derived from an electrophilic sulfone monomer.  
     
     
         19 . A polyethersulfone composition comprising structural groups derived from 9,9-bis(4-hydroxyphenyl)fluorene; and 4,4′-bis((4-chloropheyl)sulfonyl)-1,1′-biphenyl.  
     
     
         20 . The polyethersulfone composition according to  claim 19 , further comprising of structural groups derived from bis(4-chlorophenyl)sulfone.  
     
     
         21 . The polyethersulfone composition according to  claim 19 , further comprising of structural groups derived from 4,4′-biphenol.  
     
     
         22 . An article comprising the polyethersulfone composition of  claim 1 .  
     
     
         23 . A method of making a polyethersulfone composition; said method comprising: 
 (a) heating a reaction mixture comprising at least one solvent, at least one organic phase transfer catalyst, at least one dialkali metal salt of a fluorenone bisphenol VI                          wherein R 1  and R 2  are independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “a”, “b”, “c”, and “d” are independently integers from 0 to 4;    and at least one biphenyl-bissulfone VII                          wherein X 1  and X 2  are independently halogen, or nitro; R 3  and R 4  are independently at each occurrence halogen, nitro, a C 1 -C 20  aliphatic radical, a C 3 -C 20  cycloaliphatic radical, or a C 2 -C 20  aromatic radical; and “e”, “f”, “g”, and “h” are independently integers from 0 to 4 to provide a reaction product; and    (b) recovering a product polyethersulfone.    
     
     
         24 . A polyethersulfone composition consisting essentially of structural groups derived from 9,9-bis(4-hydroxyphenyl)fluorene; and 4,4′-bis((4-chloropheyl)sulfonyl)-1,1′-biphenyl.