Reactive Working Material for Use in Hydrogen Production by Decompostion of Water

Abstract

Disclosed is a reactive working material for use in a process of producing hydrogen by splitting water based on a two-step thermochemical water-splitting cycle through the utilization of solar heat, industrial waste heat or the like, which comprises a ferrite fine powder and a cubic zirconia supporting the ferrite fine powder. This reactive working material makes it possible to prevent scaling off of the ferrite fine powder from the zirconia fine powder due to volumetric changes of the ferrite fine powder during repeated use, and suppress growth of FeO grains due to repetition of melting and solidification when used as a reactive working material for a cyclic reaction under a high temperature of 1400° C. or more.

1 . A reactive working material for use in a two-step thermochemical water-splitting cycle, said reactive working material comprising a ferrite and a zirconia supporting said ferrite, wherein said ferrite-supporting zirconia is a cubic zirconia.  
     
     
         2 . The reactive working material as defined in  claim 1 , wherein said cubic zirconia contains yttria or calcia in an amount of 2 mol % or more.  
     
     
         3 . The reactive working material as defined in  claim 1 , wherein said ferrite-supporting zirconia is a composite powder of a ferrite fine powder and a zirconia fine powder.  
     
     
         4 . The reactive working material as defined in  claim 1 , wherein said ferrite-supporting zirconia comprises a zirconia porous ceramics body having a porous structure coated with a ferrite fine powder.  
     
     
         5 . A method of preparing a reactive working material for use in a two-step thermochemical water-splitting cycle, which comprises a ferrite and a zirconia supporting said ferrite, said method comprising: 
 dispersing a fully-stabilized or partially-stabilized zirconia fine powder having a particle size of 10 μm or less, in an aqueous Fe (II) salt solution, and adding an aqueous alkali hydroxide solution to said zirconia fine powder-dispersed aqueous solution to form a Fe (II) hydroxide colloid therein;    bubbling air in said colloid-containing aqueous solution to oxidize the Fe (II) hydroxide colloid; and    promoting a dissolution-precipitation reaction where the Fe (II) hydroxide colloid is dissolved in the zirconia fine powder-dispersed aqueous solution and then precipitated as Fe 3 O 4 , so as to grow Fe 3 O 4  on the dispersed zirconia fine powder.    
     
     
         6 . A method of preparing a reactive working material for use in a two-step thermochemical water-splitting cycle, which comprises a ferrite and a zirconia supporting said ferrite, said method comprising: 
 dispersing a fully-stabilized or partially-stabilized zirconia fine powder in an aqueous solution of a metal salt of Fe (II);    evaporating and drying the mixture; and    burning the dried mixture to allow the metal salt on the zirconia to be decomposed to the metal oxide; and    heating the metal oxide at a temperature of 300° C. or more.    
     
     
         7 . A hydrogen production process based on a two-step thermochemical water-splitting cycle using a reactive working material which comprises a ferrite and an yttria fully-stabilized or partially-stabilized zirconia supporting said ferrite, said process comprising two steps expressed by the following reaction formulas:  
         x/3Fe 3 O 4 +Y y Zr 1−y O 2−y/2 =Fe x Y y Zr 1−y O 2−y/2+x +x/6O 2 ; and  Fe x Y y Zr 1−y O 2−y/2+x +x/3H 2 O=x/3Fe 3 O 4 +Y y Zr 1−y O 2−y/2 +x/3H 2    
     
     
         8 . A hydrogen production process based on a two-step thermochemical water-splitting cycle using a reactive working material which comprises a ferrite and a calcia fully-stabilized or partially-stabilized zirconia supporting said ferrite, said process comprising two steps expressed by the following reaction formulas:  
         x/3Fe 3 O 4 +Ca y Zr 1−y O 2−y =Fe x Ca y Zr 1−y O 2−y+x +x/6O 2 ; and  Fe x Ca y Zr 1−y O 2−y+x +x/3H 2 O=x/3Fe 3 O 4 +Ca y Zr 1−y O 2−y +x/3H 2