Polymer composition for conductive roller, polymer composition, conductive roller, and conductive belt

Abstract

A polymer composition for a conductive roller composed of a rubber component whose main component is an epichlorohydrin rubber containing ethylene oxide at not less than 55 mol % nor more than 95 mol %. Thioureas are added to 100 g of the rubber component as a crosslinking agent at a rate not less than 0.014 mol nor more than 0.080 mol. In a compression set test of a vulcanized rubber described in JIS K6262, a compression set measured at 70° C. for 22-24 hours is less than 15%; and in a volume resistivity value test described in JIS K6911, a volume resistivity value measured at an applied voltage of 1000V is less than 10 7.5 [Ω·cm].

1 . A polymer composition for a conductive roller composed of a rubber component whose main component which is an epichlorohydrin rubber consisting of epichrohydrin-ethylene oxide-allyl glycidyl ether copolymer or epichlorohydrin-ethylene oxide copolymer containing ethylene oxide at not less than 55 mol % nor more than 95 mol %,
 wherein in a compression set test of a vulcanized rubber described in JIS K6262, a compression set measured at 70° C. for 22-24 hours is less than 15%; and in a volume resistivity value test described in JIS K6911, a volume resistivity value measured at an applied voltage of 1000V is less than 10 7.5  [Ω·cm],   and thioureas are added to 100 g of said rubber component as a crosslinking agent at a rate not less than 0.014 mol nor more than 0.080 mol,   wherein the polymer composition does not contain a lead compound,   wherein zinc oxide as an assistant crosslinking agent is added to 100 parts by weight of said rubber component at not less than 0.1 parts by weight nor more than 20.0 parts by weight, and   wherein hydrotalcite is added to 100 parts by weight of said rubber component at not less than 0.5 parts by weight nor more than 15 parts by weight.   
     
     
         2 . A polymer composition for a conductive roller composed of a rubber component which is chloroprene rubber and an epichlorohydrin rubber consisting of epichloro-hydrin-ethylene oxide copolymer containing ethylene oxide at not less than 55 mol % nor more than 95 mol %,
 wherein in a compression set test of a vulcanized rubber described in JIS K6262, a compression set measured at 70° C. for 22-24 hours is less than 15%; and in a volume resistivity value test described in JIS K6911, a volume resistivity value measured at an applied voltage of 1000V is less than 10 7.5  [Ω·cm],   and thioureas are added to 100 g of said rubber component as a crosslinking agent at a rate not less than 0.014 mol nor more than 0.080 mol,   wherein the polymer composition does not contain a lead compound,   wherein zinc oxide as an assistant crosslinking agent is added to 100 parts by weight of said rubber component at not less than 0.1 parts by weight nor more than 20.0 parts by weight, and   wherein hydrotalcite is added to 100 parts by weight of said rubber component at not less than 0.5 parts by weight nor more than 15 parts by weight.