Ferritic-austenitic stainless steel
Est. expirySep 27, 2020(expired)· nominal 20-yr term from priority
C22C 38/58C21D 2211/001C21D 2211/005C22C 38/42C22C 38/44C22C 38/001C22C 38/002C22C 38/02C22C 38/06C22C 38/46C22C 38/48C22C 38/50C22C 38/54
61
PatentIndex Score
0
Cited by
0
References
0
Claims
Abstract
A ferritic-austenitic stainless steel having a microstructure which essentially consists of 35-65 vol-% ferrite and 35-65 vol-% austenite, has a chemical composition which contains in weight-%: 0.005-0.07 C, 0.1-2.0 Si, 3-8 Mn, 19-23 Cr, 0.5-1.7 Ni, optionally Mo and/or W in a total amount of max 1.0 (Mo+W/2), optionally Cu up to max 1.0 Cu, 0.15-0.30 N, balance iron and impurities. The following conditions shall apply for the chromium and nickel equivalents: 20<Cr eq <24.5, 10<Ni eq , where, Cr eq =Cr+1.5 Si+Mo+2 Ti+0.5 Nb, Ni eq =Ni+0.5 Mn+30 (C+N)+0.5 (Cu+Co).
Claims
exact text as granted — not AI-modified1 . A ferritic-austenitic stainless steel having a microstructure which essentially consists of 35-65 vol-% ferrite and 35-65 vol-% austenite, characterised in that the steel has a chemical composition which contains in weight-%:
0.02-0.07 C 0.1-2.0 Si 3-8 Mn 19-23 Cr 1.1-1.7 Ni optionally Mo and/or W in a total amount of max 1.0 (Mo+W/2) optionally Cu up to max 1.0 Cu 0.15-0.30 N balance iron and impurities, and that the following conditions shall apply for the ferrite- and austenite formers of the alloy, respectively, i.e. for the chromium and nickel equivalents:
20<Cr eq <24.5
10<Ni eq , where
Cr eq =Cr+1.5Si+Mo+2Ti+0.5Nb
Ni eq =Ni+0.5Mn+30(C+N)+0.5(Cu+Co)
2 . A steel according to claim, characterised in that it contains max 0.05, preferably max 0 04 C.
3 . A steel according to any one of claims 1 - 2 , characterised in that it contains at least 0.2, preferably at least 0.35 Si.
4 . A steel according to any one of claims 1 - 3 , characterised in that it contains max 1.5, preferably max 1.0 Si.
5 . A steel according to any one of claims 3 and 4 , characterised in that it contains 0.35-0.80 Si.
6 . A steel according to any one of claims 1 - 5 , characterised in that it contains at least 4, suitably at least 4.5 Mn.
7 . A steel according to any one of claims 1 - 6 , characterised in that it contains max 6 Mn.
8 . A steel according to any one of claims 6 and 7 , characterised in that it contains 4.5-5.5 Mn.
9 . A steel according to any one of claims 1 - 8 , characterised in that it contains at least 20, preferably at least 20.5 Cr.
10 . A steel according to any one of claims 1 - 9 , characterised in that it contains max 23, suitably max 22.5 Cr.
11 . A steel according to any one of claims 9 and 10 , characterised in that it contains 21.0-22.0, preferably 21.2-21.8 Cr.
12 . A steel according to any one of claims 1 - 11 , characterised in that it contains 1.35-1.70 Ni.
13 . A steel according to any one of claims 1 - 12 , characterised in that it contains at least 0.1, preferably at least 0.15 Mo.
14 . A steel according to claim 13 , characterised in that it contains max 0 8 Mo, preferably max 0.65 Mo.
15 . A steel according to any one of claims 13 and 14 , characterised in that it contains 0.15-0.54 (Mo+W/2).
16 . A steel according to claims 1 - 15 , characterised in that it contains at least 0.1, preferably at least 0.15, suitably at least 0.24 Cu.
17 . A steel according to claim 16 , characterised in that it contains max 0.7 Cu.
18 . A steel according to any one of claims 16 and 17 , characterised in that it contains 0.25-0.54 Cu,
19 . A steel according claim 18 , characterised in that it contains at least 0.18 N.
20 . A steel according to any one of claims 1 - 19 , characterised in that it contains max 0.26 N.
21 . A steel according to any one of claims 19 and 20 , characterised in that it contains 0.20-0.24 N.
22 . A steel according to any one of claims 1 - 21 , characterised in that it contains 0.001-0.005 B.
23 . A steel according to any one of claims 1 - 22 , characterised in that it contains max 0.10 S.
24 . A steel according to claim 23 , characterised in that it contains max 0.002 S.
25 . A steel according to any one of claims 1 - 24 , characterised in that the coordinates of the Cr- and Ni-equivalents lie within the frame of the area A B C D A in the Schaeffler diagram in FIG. 1 , the coordinates of said points being:
Cr eq Ni eq
A
20.8
11.8
B
23.0
15.0
C
24.0
14.5
D
23.0
10.4
26 . A steel according to claim 25 , characterised in that the coordinates of the Cr- and Ni-equivalents lie within the frame of the area D E F G H D in the Schaeffler diagram in FIG. 1 , the coordinates of said points being:
Cr eq
Ni eq
D
23.0
10.4
E
22.0
11.0
F
22.0
13.5
G
22.3
14.0
H
23.0
14.0Cited by (0)