Golf ball with very low compression and high cor

Abstract

A golf ball having a very low compression and a high COR is disclosed herein. The core preferably comprises a single neodymium-catalyzed polybutadiene, and has a diameter ranging from 1.575 inch to 1.62 inch with a compression ranging from 20 to 45. The cover preferably has a thickness ranging from 0.038 inch to 0.045 inch, and a Shore D hardness ranging from 50 to 58. The golf ball preferably has a coefficient of restitution of at least 0.780, and a compression ranging from 35 to 50.

1 . A two-piece golf ball comprising:
 a core comprising a polybutadiene material, zinc diacrylate ranging from 10 to 20 weight percent of the core, zinc oxide ranging from 10 to 17 weight percent of the core, zinc stearate in an amount of 3 to 8 weight percent of the core and zinc pentachlorophenyl in an amount of 0.25 to 1.0 weight percent of the core, wherein the core has a mass ranging from 38 grams to 42 grams, a diameter ranging from 1.575 inch to 1.62 inch, and a PGA compression ranging from 20 to 45;   a cover disposed on the core, the cover composed of a material comprising a very-low modulus ionomer in an amount of 5 to 20 weight percent of the cover material, a first high acid ionomer in an amount of 20 to 30 weight percent of the cover material, a second high acid ionomer in an amount of 30 to 50 weight percent of the cover material, and an additional ionomer in an amount of 5 to 15 weight percent of the cover material, the cover having a thickness ranging from 0.038 inch to 0.045 inch, the cover material having a Shore D hardness ranging from 50 to 58;   wherein the golf ball has a diameter of at least 1.68 inches, a mass of at least 45 grams, a coefficient of restitution of at least 0.780, and a PGA compression ranging from 35 to 50.   
     
     
         2 . The two-piece golf ball according to  claim 1  wherein the core has a diameter of 1.59 inches. 
     
     
         3 . The two-piece golf ball according to  claim 1  wherein the core has a PGA compression ranging from 20 to 30. 
     
     
         4 . The two-piece golf ball according to  claim 1  wherein the cover material has a Shore D hardness of 56. 
     
     
         5 . A two-piece golf ball comprising:
 a solid core comprising a single neodymium-catalyzed polybutadiene, wherein the core has a mass ranging from 38 grams to 42 grams, a diameter ranging from 1.575 inch to 1.62 inch, and a PGA compression ranging from 20 to 45;   a cover disposed on the core, the cover composed of a material comprising at least four different ionomers, the cover having a thickness ranging from 0.038 inch to 0.045 inch, the cover material having a Shore D hardness ranging from 50 to 58;   wherein the golf ball has a diameter of at least 1.68 inches, a mass of at least 45 grams, a coefficient of restitution of at least 0.780, and a PGA compression ranging from 35 to 50.