High purity zirconia-based thermally sprayed coatings and processes for the preparation thereof

Abstract

This invention relates to thermally sprayed coatings of a high purity yttria or ytterbia stabilized zirconia powder, said high purity yttria or ytterbia stabilized zirconia powder comprising from about 0 to about 0.15 weight percent impurity oxides, from about 0 to about 2 weight percent hafnium oxide (hafnia), from about 6 to about 25 weight percent yttrium oxide (yttria) or from about 10 to about 36 weight percent ytterbium oxide (ytterbia), and the balance zirconium oxide (zirconia). Thermal barrier coatings for protecting a component such as blades, vanes and seal surfaces of gas turbine engines, made from the high purity yttria or ytterbia stabilized zirconia powders, have a density greater than 88% of the theoretical density with a plurality of vertical macrocracks homogeneously dispersed throughout the coating to improve its thermal fatigue resistance.

1 . A thermally sprayed coating of a high purity yttria or ytterbia stabilized zirconia powder for a substrate, said high purity yttria or ytterbia stabilized zirconia powder comprising from about 0 to about 0.15 weight percent impurity oxides, from about 0 to about 2 weight percent hafnium oxide (hafnia), from about 6 to about 25 weight percent yttrium oxide (yttria) or from about 10 to about 36 weight percent ytterbium oxide (ytterbia), and the balance zirconium oxide (zirconia). 
     
     
         2 . The thermally sprayed coating of  claim 1  wherein the impurity oxides comprise from about 0 to about 0.02 weight percent silicon dioxide (silica), from about 0 to about 0.005 weight percent aluminum oxide (alumina), from about 0 to about 0.01 weight percent calcium oxide, from about 0 to about 0.01 weight percent ferric oxide, from about 0 to about 0.005 weight percent magnesium oxide, and from about 0 to about 0.01 weight percent titanium dioxide. 
     
     
         3 . The thermally sprayed coating of  claim 1  wherein the impurity oxides comprise from about 0 to about 0.01 weight percent silicon dioxide (silica), from about 0 to about 0.002 weight percent aluminum oxide (alumina), from about 0 to about 0.005 weight percent calcium oxide, from about 0 to about 0.005 weight percent ferric oxide, from about 0 to about 0.002 weight percent magnesium oxide, and from about 0 to about 0.005 weight percent titanium dioxide. 
     
     
         4 . The thermally sprayed coating of  claim 1  wherein the high purity yttria or ytterbia stabilized zirconia powder comprises from about from about 0 to about 0.12 weight percent impurity oxides, from about 0 to about 1.5 weight percent hafnium oxide (hafnia), from about 6 to about 10 weight percent yttrium oxide (yttria) or from about 10 to about 16 weight percent ytterbium oxide (ytterbia), and the balance zirconium oxide (zirconia). 
     
     
         5 . The thermally sprayed coating of  claim 1  wherein the high purity yttria or ytterbia stabilized zirconia powder has a particle size of from about 1 to about 150 microns. 
     
     
         6 . The thermally sprayed coating of  claim 1  wherein the high purity yttria or ytterbia stabilized zirconia powder comprises a blend of two or more high purity yttria or ytterbia stabilized zirconia powders. 
     
     
         7 . The thermally sprayed coating of  claim 1  wherein the high purity yttria or ytterbia stabilized zirconia powder comprises from about 55 to about 95 volume percent of a first high purity yttria or ytterbia partially stabilized zirconia powder having from about 0 to about 0.15 weight percent impurity oxides, from about 0 to about 2 weight percent hafnium oxide (hafnia), from about 6 to about 8 weight percent yttrium oxide (yttria) or from about 10 to about 14 weight percent ytterbium oxide (ytterbia), and the balance zirconium oxide (zirconia), and from about 5 to about 45 volume percent of a second high purity yttria or ytterbia fully stabilized zirconia powder having from about 0 to about 0.15 weight percent impurity oxides, from about 0 to about 2 weight percent hafnium oxide (hafnia), from about 16 to about 22 weight percent yttrium oxide (yttria) or from about 25 to about 33 weight percent ytterbium oxide (ytterbia), and the balance zirconium oxide (zirconia) 
     
     
         8 . The thermally sprayed coating of  claim 1  wherein the high purity yttria or ytterbia stabilized zirconia powder comprises a blend of two or more high purity yttria or ytterbia stabilized zirconia powders that reduce the thermal conductivity of a composite coating made therefrom, and maintain the thermal shock resistance of a 6 to 8 weight percent yttria partially stabilized zirconia coating. 
     
     
         9 . The thermally sprayed coating of  claim 7  wherein the high purity yttria or ytterbia stabilized zirconia powder comprises a blend having from about 20 to about 45 volume percent of the second high purity yttria or ytterbia fully stabilized zirconia powder, and from about 55 to about 80 volume percent of the first high purity yttria or ytterbia partially stabilized zirconia powder. 
     
     
         10 . The thermally sprayed coating of  claim 1  wherein the high purity yttria or ytterbia stabilized zirconia powder comprises a composite high purity yttria or ytterbia stabilized zirconia powder, said composite high purity yttria or ytterbia stabilized zirconia powder comprising a high purity yttria or ytterbia stabilized zirconia powder having from about 0 to about 0.15 weight percent impurity oxides, from about 0 to about 2 weight percent hafnium oxide (hafnia), from about 6 to about 25 weight percent yttrium oxide (yttria) or from about 10 to about 36 weight percent ytterbium oxide (ytterbia), and the balance zirconium oxide (zirconia), said powder having a nominal average size of 20-60 microns with surface-adhered gadolinia particles having a nominal average size of 0.5 to 2 microns. 
     
     
         11 . The thermally sprayed coating of  claim 1  having a density greater than 88% of the theoretical density with a plurality of vertical macrocracks substantially homogeneously dispersed throughout the coating in which a cross-sectional area of the coating normal to the substrate exposes a plurality of vertical macrocracks extending at least half the coating thickness in length up to the full thickness of the coating and having from about 5 to about 200 vertical macrocracks per linear inch measured in a line parallel to the surface of the substrate and in a plane perpendicular to the surface of the substrate. 
     
     
         12 . The thermally sprayed coating of  claim 1  wherein the density is from 90% to 98% of the theoretical density and wherein a plurality of said vertical macrocracks extend at least two-thirds the coating thickness in length up to the full thickness of the coating. 
     
     
         13 . The thermally sprayed coating of  claim 1  wherein said coating has at least about 20 vertical macrocracks per linear inch measured in a line parallel to the surface of the substrate and in a plane perpendicular to the surface of the substrate. 
     
     
         14 . The thermally sprayed coating of  claim 1  wherein said coating has at least about 40 vertical macrocracks per linear inch measured in a line parallel to the surface of the substrate and in a plane perpendicular to the surface of the substrate. 
     
     
         15 . The thermally sprayed coating of  claim 1  wherein said coating contains one or more horizontal macrocracks extending within the coating parallel to the surface of the substrate. 
     
     
         16 . The thermally sprayed coating of  claim 1  wherein the horizontal macrocracks do not contact more than one vertical macrocrack. 
     
     
         17 . The thermally sprayed coating of  claim 1  wherein the width of the vertical macrocracks is less than 1 mil. 
     
     
         18 . The thermally sprayed coating of  claim 1  wherein the density is greater than 90% of the theoretical density and the coating has at least about 40 vertical macrocracks per linear inch measured in a line parallel to the surface of the substrate and in a plane perpendicular to the surface of the substrate. 
     
     
         19 . The thermally sprayed coating of  claim 1  wherein the high purity yttria or ytterbia stabilized zirconia powder comprises from about 0 to about 0.15 weight percent impurity oxides, from about 0 to about 2 weight percent hafnium oxide (hafnia), from about 6 to about 8 weight percent yttrium oxide (yttria) or from about 10 to about 14 weight percent ytterbium oxide (ytterbia), and the balance zirconium oxide (zirconia). 
     
     
         20 . The thermally sprayed coating of  claim 1  wherein a bond coating is deposited between the substrate and the thermally sprayed coating, said bond coating comprising (i) an alloy containing chromium, aluminum, yttrium with a metal selected from the group consisting of nickel, cobalt and iron or (ii) an alloy containing aluminum and nickel. 
     
     
         21 . The thermally sprayed coating of  claim 1  wherein a bond coating is deposited between the substrate and the thermally sprayed coating, said bond coating comprising a MCrAlY+X coating applied by a plasma spray method, where M is Ni, Co or Fe or any combination of the three elements, and X includes the addition of Pt, Ta, Hf, Re or other rare earth metals, or fine alumina dispersant particles, singularly or in combination. 
     
     
         22 . The thermally sprayed coating of  claim 1  wherein a bond coating is deposited between the substrate and the thermally sprayed coating, said bond coating comprising a MCrAlY+X coating applied by a detonation spray method, where M is Ni, Co or Fe or any combination of the three elements, and X includes the addition of Pt, Ta, Hf, Re or other rare earth metals, or fine alumina dispersant particles, singularly or in combination. 
     
     
         23 . The thermally sprayed coating of  claim 1  wherein a bond coating is deposited between the substrate and the thermally sprayed coating, said bond coating comprising a MCrAlY+X coating applied by an electroplating method, where M is Ni, Co or Fe or any combination of the three elements, and X includes the addition of Pt, Ta, Hf, Re or other rare earth metals, singularly or in combination. 
     
     
         24 . The thermally sprayed coating of  claim 1  wherein the density is at least 90% of the theoretical density and the coating has at least about 40 vertical macrocracks per linear inch measured in a line parallel to the surface of the substrate and in a plane perpendicular to the surface of the substrate. 
     
     
         25 . The thermally sprayed coating of  claim 1  having a thickness of from about 0.0025 to about 0.10 inches. 
     
     
         26 . The thermally sprayed coating of  claim 1  having horizontal crack segments, connecting any two vertical segmentation cracks, measured in the polished cross section, having a total sum length of less than 10% of the coating width. 
     
     
         27 . The thermally sprayed coating of  claim 1  having enhanced sintering resistance such that at 1200° C., density increases by less than 0.5% in 4 hours. 
     
     
         28 . The thermally sprayed coating of  claim 1  having vertical segmentation cracks that are arranged as cells in a three-dimensional coating perspective, having a mean cell width of about 0.02 inches, and a range of from about 0.005 to about 0.2 inches. 
     
     
         29 . The thermally sprayed coating of  claim 1  having a modulus in the plane of the coating of less than 0.6 MPa, and a coating cohesive strength in the direction of the coating thickness of greater than 40 MPa. 
     
     
         30 . The thermally sprayed coating of  claim 1  having, after exposure at 1200° C. for 4 hours, a modulus in the plane of the coating of less than 0.9 MPa, and a coating cohesive strength in the direction of the coating thickness of greater than 45 MPa. 
     
     
         31 . The thermally sprayed coating of  claim 1  having a thermal conductivity in a direction through the thickness of the coating that is less than 0.014 watt/centimeter at 25° C. and less than 0.0135 watt/centimeter at 500° C. 
     
     
         32 . The thermally sprayed coating of  claim 1  having, after exposure at 1200° C. for 4 hours, a thermal conductivity in a direction through the thickness of the coating that is less than 0.015 watt/centimeter at 25° C. and less than 0.014 watt/centimeter at 500° C. 
     
     
         33 . The thermally sprayed coating of  claim 1  having a particle erosion rate to 50 micron angular alumina at 20 degrees impingement and 200 feet/second velocity of less than 1 milligram per gram of erodent at 25° C. 
     
     
         34 . The thermally sprayed coating of  claim 1  having, after exposure at 1200° C. for 4 hours, a particle erosion rate to 50 micron angular alumina at 20 degrees impingement and 200 feet/second velocity of less than 0.5 milligrams per gram of erodent at 25° C. 
     
     
         35 . The thermally sprayed coating of  claim 1  having less than 3 percent monoclinic phase by x-ray diffraction methods. 
     
     
         36 . The thermally sprayed coating of  claim 1  having, after exposure at 1200° C. for 4 hours, less than 3 percent monoclinic phase by x-ray diffraction methods. 
     
     
         37 . The thermally sprayed coating of  claim 1  that is stabilized by heat treatment in vacuum or air at a temperature of 1000° C. or greater. 
     
     
         38 . A thermal barrier coating for a substrate comprising zirconia partially stabilized by yttria or ytterbia, and having a density greater than 88% of the theoretical density with a plurality of vertical macrocracks substantially homogeneously dispersed throughout the coating in which a cross-sectional area of the coating normal to the substrate exposes a plurality of vertical macrocracks extending at least half the coating thickness in length up to the full thickness of the coating and having from about 5 to about 200 vertical macrocracks per linear inch measured in a line parallel to the surface of the substrate and in a plane perpendicular to the surface of the substrate, said thermal barrier coating comprising a thermally sprayed coating of a high purity yttria or ytterbia stabilized zirconia powder, said high purity yttria or ytterbia stabilized zirconia powder comprising from about 0 to about 0.15 weight percent impurity oxides, from about 0 to about 2 weight percent hafnium oxide (hafnia), from about 6 to about 25 weight percent yttrium oxide (yttria) or from about 10 to about 36 weight percent ytterbium oxide (ytterbia), and the balance zirconium oxide (zirconia).