Method of making a sheet of building material

Abstract

A method of making a sheet of building material, useful for roofing or siding applications, and the sheet material made by such method. A mixture of a thermoplastic resin and mineral filler is prepared, the resin comprising about 10% to 40% by weight of the mixture and the filler comprising about 60% to 90% by weight. The mixture is mixed at a temperature above the melting point of the resin and is formed into a sheet at such temperature. The sheet is allowed to cool until the surface is at a temperature below the midpoint of the melting range of the thermoplastic resin, e.g. in the range of 205 to 225 degrees F. for polyethylene, at which point it is strained by passing it through calendering rollers. The sheet material made by this process, having a high concentration of mineral filler, is fire resistant, durable, ductile, of moderate weight and resistant to weathering. It can be produced using relatively inexpensive manufacturing equipment. The sheet material can incorporate a high proportion of recycled resin, such as recycled high density polyethylene.

1 . A method of making a sheet of building material for roofing or siding applications, comprising the steps of:
 (a) preparing a mixture comprising a thermoplastic resin and a mineral filler, said resin comprising about 10% to 40% by weight of said mixture and said filler comprising about 60% to 90% by weight of said mixture, said resin comprising polyethylene;   (b) mixing said mixture at a temperature above the melting range of said resin;   (c) forming said mixture into a sheet, said forming step being done at a temperature above the melting range of said resin;   (d) allowing a surface of said sheet to cool to a temperature below the midpoint of the melting range of said resin, said temperature being in the range of 205 to 225 degrees F.; and   (e) straining said sheet by calendering, rolling or pressing said sheet when said surface temperature is within said temperature range of step (d) to increase a length of said sheet by 1% to 10%.   
     
     
         2 . A method according to  claim 1 , wherein said polyethylene is a mixture of high density polyethylene and linear low density polyethylene. 
     
     
         3 . A method according to  claim 2 , wherein the weight ratio of said high density polyethylene to said linear low density polyethylene is about 3:1. 
     
     
         4 . A method according to  claim 1 , further comprising lowering said surface temperature during said step of straining. 
     
     
         5 . A method according to  claim 1 , wherein said filler is limestone. 
     
     
         6 . A method according to  claim 5 , wherein said limestone is about 100 mesh in particle size. 
     
     
         7 . A method according to  claim 1 , wherein said filler is one of dolomite, talc, silica and flyash. 
     
     
         8 . A method according to  claim 1 , wherein said thermoplastic resin comprises 10% to 35% by weight of said mixture. 
     
     
         9 . A method according to  claim 1 , wherein said resin comprises 10% to 34% by weight of said mixture and said filler comprises 66% to 90% by weight of said mixture. 
     
     
         10 . A method according to  claim 1 , wherein said mixture further comprises mica. 
     
     
         11 . A method according to  claim 10 , wherein said mica comprises 0.1% to 1.0% by weight of said mixture. 
     
     
         12 . A method according to  claim 1 , wherein said mixture further comprises one or more of carbon black, a UV stabilizer, a ductility enhancer and a fireproofing component. 
     
     
         13 . A method according to  claim 1 , wherein said step of preparing said mixture comprises heating said filler and adding said resin to said filler. 
     
     
         14 . A method according to  claim 10 , wherein said filler used to prepare said mixture is at a temperature of about 350 degrees F. 
     
     
         15 . A method according to  claim 1 , wherein said temperature of step (b) is in the range of 300 to 325 degrees F. 
     
     
         16 . A method according to  claim 1 , wherein said step of mixing is done in an open atmosphere. 
     
     
         17 . A method according to  claim 1 , wherein said step of straining comprises passing said sheet between calendering rollers. 
     
     
         18 . A method according to  claim 17 , wherein a calendering force applied by said calendering rollers is varied during the step of straining so as to cause a variation in color tone of said sheet. 
     
     
         19 . A method according to  claim 1 , further comprising the step, after step (e), of applying a protective coating to said surface of said sheet. 
     
     
         20 . A method according to  claim 1 , wherein the temperature in step (d) is in the range of 205 to 220 degrees F. 
     
     
         21 . A method according to  claim 1 , wherein the sheet produced in step (e) has a thickness of about one-quarter inch.