Powder coatings compositions

Abstract

A solid epoxy resin powder coarting composition which includes a divinylarene dioxide resin as one component; and wherein the solid epoxy resin powder coating composition can be formed by blending or reacting various other components with the divinylarene dioxide resin. For example, other components can include other epoxy resins; phenolic resins; or monomeric and/or polymeric isocyanates. The powder coating composition or formulation may advantageously provide, for example, a Fusion Bonded Epoxy coating on a substrate.

1 . A composition comprising a solid curable powder coating formulation including (i) at least one divinylarene dioxide resin, wherein the at least one divinylarene dioxide resin eposxy functional; and (ii) at least one curing component, wherein the at least one curing component is an epoxy resin, a blend of an epoxy resin and a curing catalyst, or mixtures thereof. 
     
     
         2 - 4 . (canceled) 
     
     
         5 . The composition of  claim 1 , wherein the divinylarene dioxide resin, component (i), comprises (a) a blend of a solid epoxy resin and a divinylarene dioxide compound; or (b) an epoxy oxazolidone resin prepared from a divinylarene dioxide compound and a monomeric isocyanate or a polymeric isocyanate; or (c) a phenolic hardener prepared from a divinylarene dioxide compound and a diphenol. 
     
     
         6 . The composition of  claim 1 , wherein the divinylarene dioxide compound comprises divinylbenzene dioxide. 
     
     
         7 . The composition of  claim 5 , wherein the solid epoxy resin comprises an epoxy resin prepared from a stoichiometric excess of bisphenol A diglycidyl ether and bisphenol A having a Tg of greater than about 30° C. 
     
     
         8 . The composition of  claim 5 , wherein the epoxy oxazolidone resin comprises the reaction product of a stoichiometric excess of divinylbenzene dioxide and a monomeric or polymeric isocyanate selected from toluene diisocyanate, methylenediphenyl diisocyanate, xylylene diisocyanate, isophorone diisocyanate, hexamethylene diisocyanate, and mixtures thereof. 
     
     
         9 . The composition of  claim 5 , wherein the phenolic hardener comprises the reaction product of divinylbenzene dioxide and a stoichiometric excess of a diphenol selected from the group consisting of bisphenol A, tetrabromobisphenol A, bisphenol F, hydroquinone, resorcinol, biphenol, and mixtures thereof. 
     
     
         10 . The composition of  claim 1 , wherein the catalyst comprises an imidazole. 
     
     
         11 . The composition of  claim 1 , wherein the curing component comprises a phenolic resin, or an amine, or an epoxy resin. 
     
     
         12 . The composition of  claim 1 , wherein the curing component comprises a bisphenol A type phenolic resin or a dicyandiamide. 
     
     
         13 . The composition of  claim 1 , wherein the powder coating comprises a Fusion Bonded Epoxy coating composition. 
     
     
         14 . (canceled) 
     
     
         15 . A cured coating comprising the cured composition of  claim 1 . 
     
     
         16 . An article made from the composition of  claim 1 . 
     
     
         17 . The article of  claim 16  comprising a coated substrate wherein the coating on said substrate comprises a solid divinylarene dioxide resin. 
     
     
         18 . A process for preparing a composition comprising admixing (i) at least one divinylarene dioxide resin; and (ii) at least one curing component to form a solid curable powder coating formulation. 
     
     
         19 . A process for preparing a cured coating comprising curing the composition of  claim 1  at a temperature of from about 10° C. to about 300° C.