Oxidized Carbon Blacks Treated with Polyetheramines and Coating Compositions Comprising Same

Abstract

Disclosed herein are materials and compositions comprising: an oxidized carbon black having a BET surface area ranging from 50 to 700 m 2 /g, a DBP oil adsorption number ranging from 50 to 200 mL/100 g, and a primary particle size ranging from 7 to 30 nm; and a polyetheramine comprising ethylene oxide and propylene oxide monomers, wherein the polyetheramine coats the oxidized carbon black. Also disclosed are coatings and coating compositions comprising these materials and methods of making the same.

1 . A powdered material comprising:
 an oxidized carbon black having a BET surface area ranging from 50 to 700 m 2 /g, a DBP oil adsorption number ranging from 50 to 200 mL/100 g, and a primary particle size ranging from 7 to 30 nm; and   a polyetheramine wherein said polyetheramine consists of ethylene oxide and propylene oxide monomers and one or more amine groups and wherein the polyetheramine coats the oxidized carbon black.   
     
     
         2 . The powdered material of  claim 1 , wherein the polyetheramine has a molecular weight ranging from 250 to 5,000. 
     
     
         3 . (canceled) 
     
     
         4 . The powdered material according to  claim 1 ,
 wherein the propylene oxide and ethylene oxide monomers are present in the polyetheramine in a ratio ranging from 1:2 to 9:1.   
     
     
         5 . (canceled) 
     
     
         6 . The powdered material according to  claim 1 ,
 wherein the polyetheramine is present in the powdered material in an amount ranging from 5 to 30% by weight.   
     
     
         7 . (canceled) 
     
     
         8 . The powdered material according to  claim 1 ,
 wherein the oxidized carbon black is present in the powdered material in an amount ranging from 65 to 95%.   
     
     
         9 . (canceled) 
     
     
         10 . The powdered material according to  claim 1 ,
 wherein the oxidized carbon black is formed by oxidation of unmodified carbon black.   
     
     
         11 . The powdered material according to  claim 1 ,
 wherein the material is a bulk powdered material.   
     
     
         12 . The powdered material of  claim 1 , wherein:
 the polyetheramine has the formula:   
       
         
           
           
               
               
           
         
         wherein x=1-35, y=3-30, x/y is at least 0.15, and the polyetheramine coats the oxidized carbon black. 
       
     
     
         13 . The powdered material of  claim 12 , wherein x/y is at least 0.3. 
     
     
         14 . (canceled) 
     
     
         15 . A pellet comprising:
 an oxidized carbon black having a BET surface area ranging from 50 to 700 m 2 /g, a DBP oil adsorption number ranging from 50 to 200 mL/100 g, and a primary particle size ranging from 7 to 30 nm; and   a polyetheramine wherein said polyetheramine consists of ethylene oxide and propylene oxide monomers and one or more amine groups and wherein the polyetheramine coats the oxidized carbon black.   
     
     
         16 . The pellet of  claim 15 , wherein:
 the polyetheramine has the formula:   
       
         
           
           
               
               
           
         
         wherein x=1-35, y=3-30, x/y is at least 0.15, and the polyetheramine coats the oxidized carbon black. 
       
     
     
         17 . The pellet of  claim 15 , wherein the pellet has a D50 of at least 100 μm. 
     
     
         18 - 21 . (canceled) 
     
     
         22 . A coating composition, comprising:
 an oxidized carbon black having a BET surface area ranging from 50 to 700 m 2 /g, a DBP oil adsorption number ranging from 50 to 200 mL/100 g, and a primary particle size ranging from 7 to 30 nm,   a polyetheramine wherein said polyetheramine consists of ethylene oxide and propylene oxide monomers and one or more amine groups and wherein the polyetheramine coats the oxidized carbon black and   a resin having a molecular weight of at least 10,000.   
     
     
         23 . The composition of  claim 22 , wherein the resin is selected from acrylics, polyesters, polyurethanes, alkyds, cellulose acetate butyrate, nitro cellulose, melamines, epoxies, and blends and copolymers thereof. 
     
     
         24 - 25 . (canceled) 
     
     
         26 . The composition according to  claim 22 ,
 wherein the polyetheramine has a molecular weight ranging from 500 to 5,000.   
     
     
         27 . The composition according to  claim 22 ,
 wherein the propylene oxide and ethylene oxide monomers are present in the polyetheramine in a ratio ranging from 1:2 to 9:1.   
     
     
         28 . The composition according to  claim 22 ,
 wherein the resin is present in the composition in an amount of at least 60% by weight.   
     
     
         29 . The composition according to  claim 22 ,
 wherein the oxidized carbon black is present in the composition in an amount ranging from 1% to 30% by weight.   
     
     
         30 - 32 . (canceled) 
     
     
         33 . A coating comprising:
 an oxidized carbon black having a BET surface area ranging from 50 to 700 m 2 /g, a DBP oil adsorption number ranging from 50 to 200 mL/100 g, and a primary particle size ranging from 7 to 30 nm,   a polyetheramine wherein said polyetheramine consists of ethylene oxide and propylene oxide monomers and one or more amine groups and wherein the polyetheramine coats the oxidized carbon black and   a resin selected from acrylics, polyesters, polyurethanes, alkyds, cellulose acetate butyrate, nitro cellulose, melamines, epoxies, and blends and copolymers thereof.   
     
     
         34 . (canceled) 
     
     
         35 . A method of preparing a pellet or powdered material,
 comprising:
 coating an oxidized carbon black with a polyetheramine, wherein the oxidized carbon black is obtained by oxidizing an unmodified carbon black having a BET surface area ranging from 50 to 700 m 2 /g, a DBP oil adsorption number ranging from 50 to 200 mL/100 g, and a primary particle size ranging from 7 to 30 nm, wherein said polyetheramine consists of ethylene oxide and propylene oxide monomers and one or more amine groups. 
   
     
     
         36 . The method of  claim 35 , wherein the step of coating comprises spraying the polyetheramine onto the oxidized carbon black. 
     
     
         37 . The method of  claim 35 , wherein the oxidized carbon black is obtained by oxidizing the unmodified carbon black with nitric acid. 
     
     
         38 .- 41 . (canceled)