Abstract

The present invention concerns fire retardant materials made of polymers, plastics and elastomeric-based materials comprising nanoclays intercalated with protonised silane.

1 . A fire retardant material comprising nanoclays intercalated with protonised silane, wherein said fire retardant material has an interlayer distance d001 of about 16-17.3 as measured by X-ray diffraction. 
     
     
         2 . The fire retardant material according to  claim 1 , wherein said interlayer distance d001 is 17-17.3 ANG. 
     
     
         3 . The fire retardant material according to  claim 1 , wherein said fire retardant material includes polymers, plastics or elastomeric based materials. 
     
     
         4 . The fire retardant material according to  claim 1  further comprising nanoclays intercalated with fire retardant compounds, wherein the nanoclays have at least one surface and at least one edge plane and the fire retardant compounds are bound to OH groups on the edge plane, or on Al/Si oxide on the nanoclay surface or both. 
     
     
         5 . The fire retardant material according to  claim 4 , wherein said fire retardant compounds are silanes, phosphates, brominated chemicals, amino-phosphates, or melamine-phosphates, and have high thermal stability and flame retardation properties. 
     
     
         6 . Fire retardant material according to  claim 1 , wherein the fire retardant material comprises polypropylene (PP), acrylonitrile-butadiene-styrene (ABS), polybutylene terephthalate (PBT), polystyrene (PS), polyamides (PA) or a mixture thereof. 
     
     
         7 . A method of making a fire retardant material having nanoclays intercalated with protonized silane comprising:
 reacting silane with an acid solution to obtain protonising silane;   adding the protonised silane to a dispersion of nanoclays in a solvent;   heating the solvent to a temperature up to about 70° C. to obtain a viscous slurry;   filtering the slurry to separate a solid fraction;   drying the solid fraction; and   milling the dried solid fraction into a powder.   
     
     
         8 . The method of making a fire retardant material according to  claim 7 , wherein said solvent is methanol or a mixture of methanol and water. 
     
     
         9 . The method of making a fire retardant material according to  claim 7 , further comprising after the drying step:
 grinding the solid fraction into powder;   heating the powder up to about 110° C.;   washing the heated powder with an ethanol/water mixture; and   drying the washed powder.   
     
     
         10 . The method of making the fire retardant material according to  claim 7 , further comprising:
 adding one or more fire retardant compound selected from the group consisting of silanes, phosphates, brominated chemicals, amino-phosphates, and   melamine-phosphates, wherein the fire retardant compounds have high thermal stability and flame retardation properties to the dispersion.   
     
     
         11 . The method of making the fire retardant material according to  claim 7 , further comprising:
 adding the powder to a melt of polymers, plastics and elastomeric based materials; and adding compounders to the mixture.   
     
     
         12 . The method of  claim 7 , wherein the heating step lasts 5-7 hours.