Steel strip having a low si content

Abstract

A dual phase or complex phase steel strip showing no tiger stripes. The steel strip having an ultimate tensile strength Rm classifying for 1000 MPa steel category, includes (in mass percent) C 0.09-0.19%; Mn 1.9-2.6%; Si at most 0.1%; Cr 0.4-0.8%; Mo at most 0.3%; Ni at most 0.4%; Al 0.02-1.3%; and optionally one or more of the following elements: Nb at most 0.08%; P equal to or more than 0.0005%; N equal to or less than 0.015%; Ti equal to or less than 0.1%; V equal to or less than 0.1%; B equal to or less than 0.01%; wherein the sum of Cr, Mo and Ni is at least 0.5%; the balance being Fe and inevitable impurities.

1 . A steel strip having an ultimate tensile strength Rm of at least 1000 MPa, consisting of (in mass percent)
 C 0.09-0.19%;   Mn 1.9-2.6%;   Si at most 0.1%;   Cr 0.4-0.8%;   Mo 0.003-0.3%;   Ni at most 0.4%;   Al 0.02-1.3%;   Nb at most 0.08%;   P 0 or equal to or more than 0.0005%;   N equal to or less than 0.015%;   Ti equal to or less than 0.1%;   V equal to or less than 0.1%;   B equal to or less than 0.01%;   
       wherein the sum of Cr, Mo and Ni is at least 0.5%; 
       the balance being Fe and inevitable impurities. 
     
     
         2 . The steel strip according to  claim 1 , wherein Si is at most 0.08%. 
     
     
         3 . The steel strip according to  claim 1 , wherein (in mass percent)
 C is 0.12-0.17%;   Mn is 2.10-2.50%;   Al is 0.02-0.35%.   
     
     
         4 . The steel strip according to  claim 1 , wherein
 Cr is 0.50-0.70%;   Mo is 0.003 to 0.01%;   Ni is at most 0.05%,   B is 0.0001 to 0.01%.   
     
     
         5 . The steel strip according to  claim 1 , comprising wherein
 Nb is 0.001 to 0.04%   P is 0.005 to 0.05%.   
     
     
         6 . The steel strip according to  claim 1 , having a microstructure consisting of, in area %,
 martensite 5-40%;   ferrite/upper bainite 30-95%;   lower bainite/tempered martensite 0-30%;   and pearlite less than 5%.   
     
     
         7 . The steel strip according to  claim 1 , having grain size less than 10 micrometer. 
     
     
         8 . The steel strip according to  claim 1 , coated with a coating comprising Zn. 
     
     
         9 . The steel strip according to  claim 8 , being hot dip galvanised. 
     
     
         10 . The steel strip according to  claim 8 , wherein the coating consists of, in mass percent: 0.3-4.0% Mg and 0.05-6.0% Al and at most 0.2% of one or more additional elements selected from the group of Pb, Sb, Ti, Ca, Mn, Sn, La, Ce, Cr, Ni, Zr and Bi, along with unavoidable impurities and the remainder being zinc. 
     
     
         11 . The steel strip according to  claim 2 , wherein (in mass percent)
 C is 0.12-0.17%;   Mn is 2.10-2.50%;   Al is 0.02-0.35%.   
     
     
         12 . The steel strip of  claim 1 , consisting of (in mass percent)
 C 0.12-0.17%;   Mn 2.10-2.50%;   Si 0.02-0.1%;   Cr 0.50-0.70%;   Mo 0.003 to 0.3%;   Ni at most 0.4%;   Al 0.02-0.35%;   V 0.005 to 0.1%;   B 0.0001 to 0.01,   the balance being Fe and inevitable impurities.   
     
     
         13 . The steel strip of  claim 1 , wherein
 Nb is at most 0.04%;   P is 0.0005% to 0.05%;   N is equal to or less than 0.015%;   Ti is equal to or less than 0.1%;   V is 0.005 to 0.1%; and   B is 0.0015 to 0.01%.   
     
     
         14 . A steel strip having an ultimate tensile strength Rm of at least 1000 MPa, consisting of (in mass percent)
 C 0.12-0.17%;   Mn 2.10-2.50%;   Si 0.02-0.1%;   Cr 0.50-0.70%;   Mo 0.003 to 0.01%;   Ni at most 0.05%, wherein Ni is present;   Al 0.02-0.353%;   Nb at most 0.04%;   P 0.005 to 0.05%;   N equal to or less than 0.015%;   Ti equal to or less than 0.1%;   and one or more elements selected from the group consisting of:   V 0.005 to 0.1%;   B 0.0001 to 0.01%;   
       wherein the sum of Cr, Mo and Ni is at least 0.525%; 
       the balance being Fe and inevitable impurities, 
       having a microstructure consisting of, in area %,
 martensite 5-40%; 
 ferrite/upper bainite 30-95%; 
 lower bainite/tempered martensite 0-30%; 
 and pearlite less than 5%. 
 
     
     
         15 . The steel strip of  claim 14 , wherein B is 0.0015 to 0.01%.