Abstract

A method of sterilizing a material, said method comprising the steps of: (a) introducing a solution comprising peroxyacetic acid into a hot gaseous stream to produce a peroxyacetic acid vapor; and (b) contacting such peroxyacetic acid vapor with the material to be sterilized.

1 . A method of sterilizing a material, said method comprising the steps of:
 a) introducing a solution comprising peroxyacetic acid into a hot gaseous stream to produce a peroxyacetic acid vapor; and   b) contacting such peroxyacetic acid vapor with the material to be sterilized.   
     
     
         2 . The method of  claim 1  wherein such material is selected from the group consisting of metals, plastics, polymers and elastomers. 
     
     
         3 . The method of  claim 1  wherein the peroxyacetic acid is diluted to a concentration of less than 10,000 ppm prior to being introduced into the hot gaseous stream. 
     
     
         4 . The method of  claim 3  wherein the peroxyacetic acid is diluted to a concentration of less than 4,000 ppm prior to being introduced into the hot gaseous stream. 
     
     
         5 . The method of  claim 1  wherein the hot gaseous stream is sterile air. 
     
     
         6 . The method of  claim 1  wherein the hot gaseous stream is selected from the group consisting of nitrogen, carbon dioxide and noble gases. 
     
     
         7 . The method of  claim 1  wherein the hot gaseous stream is heated to a temperature above about 250° C. prior to the introduction of the peroxyacetic acid. 
     
     
         8 . The method of  claim 1  wherein the hot gaseous stream is heated to a temperature above about 250° C. and is then cooled to a temperature of between about 80° C. and about 120° C. prior to the introduction of the peroxyacetic acid. 
     
     
         9 . The method of  claim 1  wherein the temperature of the hot gaseous stream is at least about 5° C. higher than the dew point of peroxyacetic acid. 
     
     
         10 . The method of  claim 1  wherein the contact between the peroxyacetic acid vapor and the material to be sterilized is maintained for a period of between about 15 and about 40 minutes.