Crosslinkable polymeric compositions with methyl-radical scavengers and articles made therefrom

Abstract

Crosslinkable polymeric compositions for use in, for instance, cable insulation layers, are disclosed. The crosslinkable polymeric compositions comprise an ethylene-based polymer, an organic peroxide, a crosslinking coagent, and a methyl-radical scavenger comprising at least one derivative of 2, 2, 6, 6-tetramethyl-1-piperidinyloxy (“TEMPO”), such as 4-acryloxy-2, 2, 6, 6-tetramethylpiperidine-N-oxyl, 4-allyloxy-2, 2, 6, 6-tetramethylpiperidine-N-oxyl, and bis (2, 2, 6, 6-tetramethyl-1-piperidinyloxy-4-yl) sebacate, and combinations of two or more thereof, wherein ratio of crosslinking coagent to organic peroxide is less than 1.72:1 on a molar basis. A crosslinked article prepared from a crosslinkable polymeric composition is also disclosed, the crosslinkable polymeric composition comprising, inter alia, a methyl-radical scavenger comprising at least one TEMPO derivative. In addition, a coated conductor comprising a conductive core and a polymeric layer at least partially surrounding the conductive core is disclosed, wherein at least a portion of the polymeric layer comprises the crosslinked article.

1 . A crosslinkable polymeric composition, comprising:
 an ethylene-based polymer;   an organic peroxide;   a crosslinking coagent; and   a methyl-radical scavenger comprising at least one derivative of 2,2,6,6-tetramethyl-1-piperidinyloxy,   wherein the ratio of crosslinking coagent to organic peroxide is less than 1.72:1 on a molar basis.   
     
     
         2 . The crosslinkable polymeric composition of  claim 1 , wherein the ethylene-based polymer is selected from the group consisting of low-density polyethylene, linear-low-density polyethylene, very-low-density polyethylene, and combinations of two or more thereof. 
     
     
         3 . The crosslinkable polymeric composition according to  claim 1 , wherein the organic peroxide is selected from the group consisting of dicumyl peroxide, tert-butyl peroxybenzoate, di-tert-amyl peroxide, bis(alpha-t-butyl-peroxyisopropyl) benzene, isopropylcumyl t-butyl peroxide, t-butylcumylperoxide, di-t-butyl peroxide, 2,5-bis(t-butylperoxy)-2,5-dimethylhexane, 2,5-bis(t-butylperoxy)-2,5-dimethylhexyne-3, 1,1-bis(t-butylperoxy)-3,3,5-trimethylcyclohexane, isopropylcumyl cumylperoxide, butyl 4,4-di(tert-butylperoxy) valerate, di(isopropylcumyl) peroxide, and combinations of two or more thereof. 
     
     
         4 . The crosslinkable polymeric composition according to  claim 1 , wherein the crosslinking coagent is selected from the group consisting of triallyl isocyanurate, triallyl cyanurate, triallyl trimellitate, trimethylolpropane triacrylate, N2,N2,N4,N4,N6,N6-hexaallyl-1,3,5-triazine-2,4,6-triamine and combinations of two or more thereof. 
     
     
         5 . The crosslinkable polymeric composition according to  claim 1 , wherein the crosslinking coagent comprises a blend of crosslinking coagents. 
     
     
         6 . The crosslinkable polymeric composition according to  claim 1 , wherein the at least one derivative of 2,2,6,6-tetramethyl-1-piperidinyloxy is selected from the group consisting of 4-acryloxy-2,2,6,6-tetramethylpiperidine-N-oxyl, 4-allyloxy-2,2,6,6-tetramethylpiperidine-N-oxyl, and bis(2,2,6,6-tetramethyl-1-piperidinyloxy-4-yl) sebacate, and combinations of two or more thereof. 
     
     
         7 . The crosslinkable polymeric composition of  claim 1 , further comprising one or more additives including, but not limited to, scorch retardants, antioxidants, processing aids, fillers, coupling agents, ultraviolet absorbers or stabilizers, antistatic agents, nucleating agents, slip agents, plasticizers, lubricants, viscosity control agents, tackifiers, anti-blocking agents, surfactants, extender oils, acid scavengers, flame retardants, and metal deactivators. 
     
     
         8 . The crosslinkable polymeric composition of  claim 1 , wherein the ethylene-based polymer is present in an amount ranging from 90 to 99.9 weight percent, based on the entire crosslinkable polymeric composition weight, wherein the organic peroxide is present in an amount of less than 3 weight percent, based on the entire crosslinkable polymeric composition weight, wherein the crosslinking coagent is present in an amount ranging from 0.2 to 1 weight percent, based on the entire crosslinkable polymeric composition weight, wherein the methyl-radical scavenger is present in an amount ranging from 0.05 to 1 weight percent, based on the entire crosslinkable polymeric composition weight. 
     
     
         9 . A crosslinked polymeric article prepared from the crosslinkable polymeric composition according to  claim 1 . 
     
     
         10 . A cable core, comprising:
 a conductor;   a first polymeric semiconductive layer at least partially surrounding the conductor;   an insulation layer at least partially surrounding the first polymeric semiconductive layer and comprising the crosslinked polymeric article of  claim 9 ; and   a second semiconductive layer at least partially surrounding the insulation layer.