Tetrafluoroethylene/hexafluoropropylene copolymer, and electric wire

Abstract

Provided is a tetrafluoroethylene/hexafluoropropylene copolymer which is less likely to form a lump, or is less likely to form a large lump even if a lump is formed, during the formation of an electric wire. The tetrafluoroethylene/hexafluoropropylene copolymer has a melt flow rate measured at 372° C. of 35.0 to 45.0 g/10 minutes and a swell of −8.0% to 5.0%, the sum of the numbers of —CF2H groups and unstable end groups being 120 or less per 1×106 carbon atoms.

1 . An electric wire comprising:
 a core wire, and   a coating including a tetrafluoroethylene/hexafluoropropylene copolymer having a melt flow rate measured at 372° C. of 35.0 to 45.0 g/10 minutes and a die swell of −8.0% to 5.0%, and   the sum of the numbers of —CF 2 H groups and unstable end groups being 120 or less per 1×10 6  carbon atoms,   wherein die swell is measured by extruding the copolymer maintained at 372° C.±0.5° C. through an orifice having a diameter of 1 mm under a load of 5000 g with a piston to obtain an extruded strand, allowing the extruded strand to cool to room temperature, measuring the diameter of the cooled strand at a portion 5±1 mm from a first extruded tip portion of the strand, obtaining an average of the diameters of three strands obtained in the same period, and calculating the die swell according to the following formula:
   die swell (%)=[(SD−OD)/OD]×100
 
   where SD: the diameter of strand (average of the diameters of three strands) and OD: the diameter of the orifice (1 mm).   
     
     
         2 . The electric wire according to  claim 1 , which is a foamed electric wire. 
     
     
         3 . The electric wire according to  claim 1 , wherein the sum of the numbers of —CF 2 H groups and unstable end groups is 50 or less per 1×10 6  carbon atoms. 
     
     
         4 . The electric wire according to  claim 1 , wherein the die swell is −6.0% to 4.9%. 
     
     
         5 . The electric wire according to  claim 1 , wherein the sum of the numbers of —CF 2 H groups and unstable end groups is 20 or less per 1×10 6  carbon atoms. 
     
     
         6 . The electric wire according to  claim 1 , wherein the tetrafluoroethylene/hexafluoropropylene copolymer has a heating weight loss of 0.1% by weight or less after heating at 372° C. for 30 minutes. 
     
     
         7 . The electric wire according to  claim 1 , wherein the tetrafluoroethylene/hexafluoropropylene copolymer has a melting point of 245° C. to 280° C., and
 wherein melting point is determined as being a temperature corresponding to a peak obtained by measurement using a differential scanning calorimeter at a temperature rise rate of 10° C./min. 
 
     
     
         8 . The electric wire according to  claim 1 , wherein the tetrafluoroethylene/hexafluoropropylene copolymer comprises a polymerized unit derived from tetrafluoroethylene, a polymerized unit derived from hexafluoropropylene, and a polymerized unit derived from a perfluoro(alkyl vinyl ether). 
     
     
         9 . The electric wire according to  claim 8 , wherein the perfluoro(alkyl vinyl ether) is perfluoro(propyl vinyl ether).