Use of geopolymeric additive in combination with non-brominated flame retardant in polymer foams

Abstract

The invention relates to the use of i) geopolymer and ii) non-brominated, phosphorus- and/or nitrogen-based flame retardants for improving the self-extinguishing properties of a composition comprising polymer. The polymer may be a vinyl aromatic polymer, and may be in a granulate or foam.

1 . Use of
 i) one or more geopolymer additives, wherein the geopolymer additive is
 a) a geopolymer; 
 b) a combination of a geopolymer with an athermanous additive; or 
 c) a geopolymer composite derived from geopolymer and comprising athermanous additive, 
   and   ii) one or more non-brominated flame retardants selected from
 a) phosphorus-based flame retardants, 
 b) nitrogen-based flame retardants, and 
 c) phosphorus/nitrogen-based flame retardants, 
   for improving the self-extinguishing properties of a composition comprising vinyl aromatic polymer.   
     
     
         2 . The use of  claim 1 , wherein the composition is expandable vinyl aromatic polymer granulate, or an expanded foam product made thereof,
 which composition comprises
 vinyl aromatic polymer prepared from styrene monomer with optional incorporation of one or more vinyl comonomers and 
 c) 0.01-50 wt. % (by polymer weight, including solid and, if any, liquid additives, but exclusive of propellant) of geopolymer composite in powder form, with a particle size in a range of from 0.01 μm to 200 μm and a BET surface in a range of from 0.01 to 10,000 m 2 /g. 
   
     
     
         3 . The use of  claim 1 , wherein the composition does not comprise polymeric brominated flame retardant,
 preferably wherein the composition does not comprise brominated flame retardant,   in particular wherein the composition does not comprise halogenated flame retardant.   
     
     
         4 . The use of  claim 1 , wherein the athermanous additive is one or more selected from the group consisting of
 (1) carbon-based athermanous additives,   (2) metal athermanous additives,   (3) metal oxide athermanous additives, and   (4) metal sulfide athermanous additives.   
     
     
         5 . The use of  claim 4 , wherein the carbon-based athermanous additive is selected from carbon black, coke, graphitized carbon black, graphite, graphite oxides, anthracite, graphene, and graphene oxide. 
     
     
         6 . The use of  claim 4 , wherein the metal athermanous additive is selected from copper, bismuth, nickel, iron, tungsten, silver, cadmium, cobalt, tin, zinc. 
     
     
         7 . The use of  claim 4 , wherein the metal oxide athermanous additive is selected from oxides of the metals of groups TIM, IV-VIIIA, and I-VB of the periodic table. 
     
     
         8 . The use of  claim 1 , wherein the phosphorus-based flame retardant a) is selected from red phosphorus, organic and inorganic phosphates, phosphonates, phosphinates, and phosphoramidates, preferably wherein
 the organic phosphate is selected from triphenyl phosphate (TPP), resorcinol bis(diphenylphosphate) (RDP), bisphenol A bis(diphenylphosphate) (BADP), tricresyl phosphate (TCP), and resorcinol bis(2,6-dixylenylphosphate) (RDX),   the phosphinate is selected from aluminium phosphinates, calcium phosphinates and zinc phosphinates, and   the phosphoramidate is 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO).   
     
     
         9 . The use of  claim 1 , wherein the nitrogen-based flame retardant b) is selected from hindered amine stabilizer, ammonium octamolybdate, melamine octamolybdate, benzoguanamine, tris(hydroxyethyl) isocyanurate, allantois, glycoluril, melamine, melamine cyanurate, dicyandiamide, guanidine, carbodiimides, condensation products of melamine, and derivatives thereof. 
     
     
         10 . The use of  claim 1 , wherein the phosphorus/nitrogen-based flame retardant c) is selected from melamine phosphate, melamine pyrophosphate, melamine polyphosphate ammonium polyphosphate, and ethylene diamine phosphate. 
     
     
         11 . The use of  claim 1 , wherein the non-brominated flame retardant is a non-halogenated flame retardant. 
     
     
         12 . The use of  claim 1 , wherein the geopolymer or geopolymer composite has been modified with one or more water-soluble compounds,
 preferably wherein the water-soluble compound is selected from phosphorus compounds, nitrogen compounds, copper compounds, silver compounds, zinc compounds, tin compounds, and magnesium compounds,   more preferably wherein the modification is with a phosphorus compound,   in particular wherein the modification is with a phosphorus compound selected from phosphoric acid and ammonium polyphosphate.   
     
     
         13 . The use of  claim 1 , wherein the geopolymer or geopolymer composite has an average particle size (D50) in the range of 0.1 to 10 μm. 
     
     
         14 . A process for the production of expandable polymer granulate by an extrusion or a suspension process, the process comprising the addition of
 i) one or more geopolymer additives, wherein the geopolymer additive is
 a) a geopolymer; 
 b) a combination of a geopolymer with an athermanous additive; or 
 c) a geopolymer composite derived from geopolymer and comprising athermanous additive, 
   and   ii) one or more non-brominated flame retardants selected from
 a) phosphorus-based flame retardants, 
 b) nitrogen-based flame retardants, and 
 c) phosphorus/nitrogen-based flame retardants; 
   wherein the polymer is a vinyl aromatic polymer.   
     
     
         15 . Composition comprising one or more polymers, the composition further comprising
 i) one or more geopolymer additives, wherein the geopolymer additive is
 a) a geopolymer; 
 b) a combination of a geopolymer with an athermanous additive; or 
 c) a geopolymer composite derived from geopolymer and comprising athermanous additive, 
   and   ii) one or more non-brominated flame retardants selected from
 a) phosphorus-based flame retardants, 
 b) nitrogen-based flame retardants, and 
 c) phosphorus/nitrogen-based flame retardants, 
   wherein the composition is in the form of an expandable granulate, wherein the polymer is a vinyl aromatic polymer, the granulate further comprising one or more propellants.   
     
     
         16 . Composition comprising one or more polymers, the composition further comprising
 i) one or more geopolymer additives, wherein the geopolymer additive is
 d) a geopolymer; 
 e) a combination of a geopolymer with an athermanous additive; or 
 f) a geopolymer composite derived from geopolymer and comprising athermanous additive, 
   and   ii) one or more non-brominated flame retardants selected from
 d) phosphorus-based flame retardants, 
 e) nitrogen-based flame retardants, and 
 f) phosphorus/nitrogen-based flame retardants, 
   wherein the composition is in the form of expanded vinyl polymer foam, and the vinyl polymer is vinyl aromatic polymer,   the foam having
 a density of from 8 to 30 kg/m 3 , and 
 a thermal conductivity (as measured according to ISO 8301) of from 25 to 35 mW/K·m. 
   
     
     
         17 . The expanded vinyl polymer foam of  claim 16 , obtainable by expansion of a granulate, comprising a composition comprising one or more polymers, the composition further comprising
 i) one or more geopolymer additives, wherein the geopolymer additive is
 a) a geopolymer; 
 b) a combination of a geopolymer with an athermanous additive; or 
 c) a geopolymer composite derived from geopolymer and comprising athermanous additive, 
   and   ii) one or more non-brominated flame retardants selected from
 a) phosphorus-based flame retardants, 
 b) nitrogen-based flame retardants, and 
 c) phosphorus/nitrogen-based flame retardants, 
   wherein the composition is in the form of an expandable granulate, wherein the polymer is a vinyl aromatic polymer, the granulate further comprising one or more propellants.   
     
     
         18 . (canceled)