Process with photopolymerization for preparing microcapsules of controlled size

Abstract

A method for preparing solid microcapsules by adding, with stirring, a composition C1, having at least one active ingredient, in a photocrosslinkable polymeric composition C2, to obtain an emulsion (E1), adding, with stirring of the emulsion (E1) in a composition C3, the viscosity of the composition C3 being greater than 2000 mPa·s at 25° C., to obtain a double emulsion (E2), applying shear to the emulsion (E2), the applied shear rate being less than 1000 s−1, to obtain a double emulsion (E3), and polymerizing by photopolymerization of the composition C2.

1 . A method for preparing solid microcapsules comprising the steps of:
 a) adding, with stirring, a composition C1, comprising at least one active ingredient, in a photocrosslinkable polymer composition C2, the compositions C1 and C2 not being miscible with each other,   wherein an emulsion (E1) comprising drops of composition C1 dispersed in composition C2, is obtained;   b) adding, with stirring, the emulsion (E1) in a composition C3, the compositions C2 and C3 not being miscible with each other,   the viscosity of the composition C3 being greater than the viscosity of the emulsion (E1), and being greater than 2,000 mPa·s at 25° C.,   wherein a double emulsion (E2) comprising drops dispersed in the composition C3, is obtained;   c) applying shear to the emulsion (E2), the applied shear rate being less than 1000 s −1 ,   wherein a double emulsion (E3) is obtained comprising controlled-size drops dispersed in the composition C3; and   d) polymerizing by photopolymerization the composition C2, wherein solid microcapsules dispersed in the composition C3 are obtained.   
     
     
         2 . The method according to  claim 1 , wherein the composition C2 is a liquid the viscosity of which at 25° C. is between 500 mPa·s and 100 000 mPa·s. 
     
     
         3 . The method according to  claim 1 , wherein the composition C2 comprises at least one monomer or polymer, at least one crosslinking agent, and at least one photoinitiator. 
     
     
         4 . The method according to  claim 3 , wherein the composition C2 comprises from 0.001% to 70% by weight of crosslinking agent relative to the total weight of composition C2. 
     
     
         5 . The method according to  claim 1 , wherein the active ingredient is solubilized in the composition C1, or is dispersed in the form of solid particles in the composition C1. 
     
     
         6 . The method according to  claim 1 , wherein the composition C3 comprises at least one branched polymer, and/or at least one polymer of molecular weight greater than 5,000 g.mol −1 , and/or solid particles such as silicates. 
     
     
         7 . The method according to  claim 1 , wherein the viscosity of composition C3 at 25° C. is between 1000 mPa·s and 100,000 mPa·s. 
     
     
         8 . Method according to  claim 1 , wherein the shear rate applied in step c) is between 10 s −1  and 1000 s −1 . 
     
     
         9 . The method according to  claim 1 , wherein step d) comprises exposing the emulsion (E3) to a light source capable of initiating the photopolymerization of the composition C2. 
     
     
         10 . The method according to  claim 9 , wherein the light source is a UV light source. 
     
     
         11 . The method according to  claim 6 , wherein the composition C3 comprises at least one branched polymer with a molecular weight greater than 5000 g.mol − .