Fabric and method of producing the same

Abstract

A fabric includes a fabric body and a backing resin layer laminated on a rear surface of the fabric body. The fabric body includes a fluorine-containing organic compound adhered to at least the surface thereof, and the fluorine-containing organic compound has six carbon atoms and at least one fluorine atom. The backing resin layer contains a resin, a flame retardant, and an organic fluorine based oil repellent in which the carbon number is six.

1 - 13 . (canceled) 
     
     
         14 . A fabric comprising:
 a fabric body; and   a backing resin layer applied to a rear surface of the fabric body,   
       wherein:
 the fabric body contains a fluorine-containing organic compound adhered to at least a surface of the fabric body; and 
 
       the backing resin layer contains a resin, a flame retardant, and an anionic or nonionic organic fluorine based oil repellent. 
     
     
         15 . The fabric as recited in  claim 16 , wherein the fluorine-containing organic compound is in a range of 0.6 parts by mass to 1.8 parts by mass in adhesive amount with respect to 100 parts by mass of the fabric body. 
     
     
         16 . The fabric as recited in  claim 16 , wherein the organic fluorine based oil repellent in the backing resin layer is in a range of 0.8 mass % to 7 mass % in content rate. 
     
     
         17 . A method of producing a fabric, comprising:
 immersing a fabric body in a processing solution containing a fluorine-containing organic compound, and then heat-drying the fabric body at a temperature of 100° C. to 225° C.; and   
       applying a backing resin layer containing a resin, a flame retardant, and an anionic or nonionic organic fluorine based oil repellent on one surface of the fabric body. 
     
     
         18 . A method of producing a fabric, comprising:
 immersing a fabric body in a processing solution containing a fluorine-containing organic compound and then heat-drying the fabric body at a temperature of 100° C. to 225° C.;   water washing the fabric body after the heat-drying with hot water at a temperature of 70° C. to 100° C., and then drying the fabric body at a temperature of 100° C. to 135° C.; and   applying a backing resin layer containing a resin, a flame retardant, and an anionic or nonionic organic fluorine based oil repellent on one surface of the fabric body obtained through the washing and the drying.   
     
     
         19 . The method of producing a fabric as recited in  claim 19 , wherein after laminating the backing resin layer on one side of the fabric body, the drying by heating is performed by setting a drying time to 1.6 minutes to 2.6 minutes. 
     
     
         20 . The method of producing a fabric as recited in  claim 20 , wherein after applying the backing resin layer on one side of the fabric body, the drying by heating is performed by setting a drying time to 1.6 minutes to 2.6 minutes. 
     
     
         21 . The fabric as in  claim 16 , wherein the resin of the backing resin layer is a urethane resin, polyester resin or acrylic based resin. 
     
     
         22 . The fabric as in  claim 16 , wherein the fluorine-containing organic compound is a cationic fluorine-containing organic compound.