Emulsion foam reducer for wet processing of cellulose or wood-based products or in food processing

Abstract

Methods are provided for defoaming water used in processing of various products such as cellulose or wood-based products or in food processing which is formed by reacting a fatty acid with a compound selected from the group consisting of ammonia, sodium, potassium and combinations thereof so as to form a water soluble soap, dispersing the water soluble soap in water, and homogenizing the dispersed water soluble soap with hydrophobic oil or hydrocarbon oil to produce the emulsion. Methods for preparing an emulsion used in this process are also provided. The emulsion is advantageous in that it can improve water resistance and/or reduce the use of water resistant additives during processing of cellulose or wood-based products or food-grade products.

What is claimed is: 
     
         1 . A method of reducing foam and/or reducing water absorption in wet processing of manufactured board, paperboard or other cellulose or wood-based product, said method comprising:
 providing an emulsion composition having emulsifiers that undergo an exchange reaction with a hardness ion used in the wet process, said wet process containing hardness ions and used in processing of manufactured board, paperboard or other cellulose or wood based product; and   adding said emulsion composition to processing water used in said wet process in a manner so as to distribute said emulsion into said wet process so as to allow emulsifiers in said emulsion composition to react with said hardness ions in the processing water so as to form hydrophobic particles and thus change the emulsifiers into a water resistant compound while also suppressing or eliminating foam in the processing water.   
     
     
         2 . The method according to  claim 1  further comprising drying said manufactured board, paperboard or other cellulose or wood-based product processed by said method so as to obtain a water-resistant manufactured board, paperboard or other cellulose or wood-based product so that it absorbs less water when submerged in water. 
     
     
         3 . The method according to  claim 1  wherein the hardness ion is selected from the group consisting of magnesium, calcium, aluminum, iron, and zinc. 
     
     
         4 . The method according to  claim 1  wherein the product is insulation board or paper. 
     
     
         5 . The method according to  claim 1  wherein said hardness ion is present in sufficient concentration so that an exchange reaction to take place 
     
     
         6 . A method of making an emulsion comprising:
 reacting a fatty acid, or other emulsifiers that undergo an exchange reaction, with ammonia, amines, sodium or potassium hydroxide, or combinations thereof so that said fatty acid or other emulsifiers no longer act as emulsifiers, soaps, or detergents when added to a wet process containing hardness ions and used in processing of manufactured board, paperboard or other cellulose or wood based product.   adding a hydrophobic oil, a hydrocarbon oil, or a hydrophobic hydrocarbon wax to said fatty acid or other emulsifiers and homogenizing until an emulsion is formed.   
     
     
         7 . The method of making an emulsion according to  claim 6 , wherein the hydrocarbon oil is a non-polar hydrocarbon oil. 
     
     
         8 . The method of making an emulsion according to  claim 6 , wherein the hydrophobic oil is a hydrophobic hydrocarbon oil. 
     
     
         9 . The method of making an emulsion according to  claim 6 , further comprising:
 adding said emulsion to a wet process containing hardness ions and used in processing of manufactured board, paperboard or other cellulose or wood based product; and   drying a product obtained by said wet process to obtain a finished product with greater water resistance.   
     
     
         10 . The method of making an emulsion according to  claim 9 , wherein the finished product is insulting board or paper. 
     
     
         11 . The method of making an emulsion according to  claim 6 , wherein the fatty acid is selected from the group consisting of stearic acid, caprylic acid, capric acid, lauric acid, myristic acid, palmitic acid, arachidic acid, behenic acid, lignoceric acid, cerotic acid, palmitoleic acid, sepienic acid, oleic acid, elaidic acid, vaccennic acid, linoleic acid, linolaidic acid, arachidonic acid, eicosapentaenoic acid, erucic acid, docosahexexaenoic acid, tall oil and mixtures thereof. 
     
     
         12 . A method of improving water resistance in a finished product obtained by processing of manufactured board, paperboard or other cellulose or wood-based product using a wet process, said method comprising:
 providing an emulsion with a water-soluble soap that undergoes an exchange reaction in processing water of said wet process with a hardness ion of calcium, magnesium, iron, aluminum, or zinc and thereby no longer acts as soap;   dispersing said water-soluble soap in said processing water and homogenizing the soap and said processing water with a material selected from the group consisting of hydrophobic hydrocarbon wax, slack wax, paraffin wax, paraffin oil, hydrocarbon oil, and hydrophobic hydrocarbon oil;   adding said emulsion to said processing water to distribute emulsion into the wet process so as to allow soap in said emulsion to undergo an exchange reaction with hardness ions in the processing water so as to form hydrophobic particles or compounds and thereby change said soap into a water resistant compound in said processing water; and   drying or pressing the manufactured board, paperboard, or other cellulose or wood-based product obtained in said method so as to improve water resistance.   
     
     
         13 . The method according to  claim 12  wherein said method also suppresses, reduces, or eliminates foam in the processing water. 
     
     
         14 . The method according to  claim 12  wherein said hardness ion is present in sufficient concentration so that an exchange reaction to take place 
     
     
         15 . The method according to  claim 12  wherein the pH of the emulsion is between 6 and 9. 
     
     
         16 . The method according to  claim 12  wherein the pH of the emulsion is greater than 6. 
     
     
         17 . A method of reducing foam in industrial water used it a wet process to obtain manufactured board, paperboard, or other cellulose or wood-based product comprising:
 providing an emulsion having emulsifiers or a water-soluble soap that undergoes an exchange reaction with a hardness ion used in the wet process, said wet process containing hardness ions used in processing of manufactured board, paperboard or other cellulose or wood based product, said exchange reaction forming a water-soluble salt and an insoluble organometallic solid which acts as a defoamer;   adding said emulsion to industrial water used in said wet process in a manner so as to distribute said emulsion into said wet process so as to allow emulsifiers in said emulsion to react with said hardness ions in the processing water so as to form hydrophobic particles and thus change the emulsifiers into a water resistant compound while also suppressing or eliminating foam in the industrial water during said wet process.   
     
     
         18 . The method of  claim 17  wherein the hardness ion is selected from the group consisting of calcium, magnesium, iron, aluminum, and zinc. 
     
     
         19 . The method of  claim 17  wherein said method results in the reduction of water absorption of a product produced by the wet processing of manufactured board, paperboard or other cellulose or wood based product. 
     
     
         20 . The method of  claim 19  wherein said product is insulated board or paper.