Films comprising blends of polyurethanes and copolyester elastomers useful as auto wraps

Abstract

Thermoplastic films are disclosed that include a thermoplastic polymer layer comprising a thermoplastic polyurethane polymer and a copolyester polyether polymer, and a patterned adhesive layer. The thermoplastic films, when tested by a 25% Heat Relaxation Test at a thickness of about 0.006 inches, exhibits a final load from about 0.02 to about 0.3 pounds force; and when tested by a 25% Elastic Recovery test, exhibits a residual strain at one minute of 2% or greater.

1 . A thermoplastic film, comprising:
 a. a thermoplastic polymer layer comprising:
 i. a thermoplastic polyurethane polymer comprising the reaction product of:
 1. an aliphatic diisocyanate, 
 2. an aliphatic polyol, and 
 3. a chain extending agent; and 
 
 ii. a copolyester polyether polymer comprising the reaction product of:
 1. an aliphatic diacid; 
 2. an aliphatic diol; 
 3. an aliphatic polyether polyol; and 
 4. a branching agent 
 
 wherein the thermoplastic polyurethane polymer is present in the thermoplastic polymer layer in an amount from about 65 to about 98 percent by weight; and 
   b. a patterned adhesive layer,   wherein the thermoplastic film:
 when tested by a 25% Heat Relaxation Test at a thickness of about 0.006 inches, exhibits a final load from about 0.05 to about 0.30 pounds force; and 
 when tested by a 25% Elastic Recovery test, exhibits a residual strain at one minute of 2% or greater. 
   
     
     
         2 . The thermoplastic film of  claim 1 , wherein the thermoplastic film further comprises a colored layer, positioned between the thermoplastic layer and the patterned adhesive layer. 
     
     
         3 . The thermoplastic film of  claim 1 , wherein the thermoplastic film further comprises a colored layer, positioned between the thermoplastic layer and a protective topcoat. 
     
     
         4 . The thermoplastic film of  claim 1 , wherein the thermoplastic film further comprises a protective topcoat provided with a pigment, positioned on the thermoplastic polymer layer. 
     
     
         5 . The thermoplastic film of  claim 1 , wherein the patterned adhesive layer comprises a pigment. 
     
     
         6 . The thermoplastic film of  claim 1 , wherein the thermoplastic layer comprises a pigment. 
     
     
         7 . The thermoplastic film of  claim 1 , wherein the thermoplastic film, when tested by ASTM D-412, exhibits a stress at 5% strain of no greater than 700 psi. 
     
     
         8 . The thermoplastic film of  claim 1 , wherein the thermoplastic film, when tested by ASTM D-412, exhibits a stress at 5% strain of from about 200 to about 700 psi. 
     
     
         9 . The thermoplastic film of  claim 1 , wherein the thermoplastic film, when tested by a 25% Heat Relaxation Test at a thickness of about 0.006 inches, exhibits a final load from about 0.10 to about 0.20 pounds force. 
     
     
         10 . The thermoplastic film of  claim 1 , wherein the thermoplastic film, when tested by an Impact Force Attenuation Test, exhibits an attenuated load, and when tested by ASTM D-412, exhibits a tensile load per inch at 5% strain, and wherein a ratio of the attenuated load to the tensile load per inch at 5% strain is from about 80:1 to about 300:1. 
     
     
         11 . The thermoplastic film of  claim 1 , wherein the thermoplastic polyurethane polymer comprises a soft segment and a hard segment, and wherein the soft segment comprises from about 40 to about 50 percent by weight of the thermoplastic polyurethane polymer. 
     
     
         12 . The thermoplastic film of  claim 1 , wherein the copolyester polyether polymer comprises poly(cyclohexylene dimethylene cyclohexanedicarboxylate), glycol and acid comonomer (PCCE). 
     
     
         13 . The thermoplastic film of  claim 1 , wherein the thermoplastic polyurethane polymer is present in the thermoplastic polymer layer in an amount from about 70 to about 97 percent by weight. 
     
     
         14 . The thermoplastic film of  claim 1 , wherein the thermoplastic polyurethane layer further comprises one or more of: an aliphatic polyether thermoplastic polyurethane; ethylene vinyl acetate (EVA); polyvinyl chloride; a thermoplastic polyamide, a thermoplastic polyolefin elastomer, a thermoplastic styrene block copolymer; an aromatic thermoplastic copolyester ether elastomer; or a polyvinyl acetal. 
     
     
         15 . The thermoplastic film of  claim 1 , wherein the thermoplastic film is visually clear. 
     
     
         16 . The thermoplastic film of  claim 1 , wherein the aliphatic diisocyanate comprises at least 80 mol % of one or more of 4,4′-Methylene dicyclohexyl diisocyanate, hexamethylene diisocyanate, or isophorone diisocyanate. 
     
     
         17 . The thermoplastic film of  claim 1 , wherein the aliphatic polyol of the thermoplastic polyurethane polymer has a Mw from about 750 to about 2,000. 
     
     
         18 . The thermoplastic film of  claim 1 , wherein the chain extending agent comprises a diol having from two to ten carbon atoms. 
     
     
         19 . The thermoplastic film of  claim 1 , wherein the thermoplastic polyurethane polymer or thermoplastic polyurethane polymer blend has a Tg from about −30° C. to about 60° C. 
     
     
         20 . The thermoplastic film of  claim 1 , wherein the thermoplastic polyurethane has a weight average molecular weight from 50,000 daltons to 400,000 daltons. 
     
     
         21 . The thermoplastic film of  claim 1 , wherein the thermoplastic polyurethane polymer comprises residues of hexamethylene diisocyanate, 1,4-butanediol, and caprolactone. 
     
     
         22 . The thermoplastic film of  claim 1 , wherein the thermoplastic film further comprises a protective topcoat on a side of the film opposite the patterned adhesive layer. 
     
     
         23 . The thermoplastic film of  claim 1 , wherein the copolyester polyether polymer has a Tg from about −70 C to about 50 C. 
     
     
         24 . The thermoplastic film of  claim 1 , wherein the copolyester polyether polymer has an inherent viscosity (IhV) from about 0.85 to about 1.40. 
     
     
         25 . The thermoplastic film of  claim 1 , wherein the aliphatic diacid of the copolyester polyether polymer comprises cyclohexane dicarboxylic acid. 
     
     
         26 . The thermoplastic film of  claim 1 , wherein the aliphatic diol in the copolyester polyether polymer comprises cyclohexane dimethanol. 
     
     
         27 . An article coated with the thermoplastic film of  claim 1 . 
     
     
         28 . The article of  claim 27 , wherein the article comprises one or more of an automobile, a truck, or a train. 
     
     
         29 . A method of applying the thermoplastic film of  claim 1 , the method comprising:
 a. exposing the patterned adhesive layer;   b. tacking the patterned adhesive layer of the thermoplastic film to at least one location on the substrate;   c. stretching the thermoplastic film and tacking the patterned adhesive layer to another location on the substrate;   d. smoothing out the thermoplastic film using one or more of a hand, a gloved hand, or a squeegee so that the thermoplastic film conforms to the substrate; and   e. wrapping the thermoplastic film around at least one edge of the substrate so as to hide an underlying color of the substrate.   
     
     
         30 . The method of  claim 29 , wherein the thermoplastic film is heated during the method. 
     
     
         31 . The method of  claim 29 , wherein the thermoplastic film is heated after the thermoplastic film is applied to the substrate, to accomplish one or more of: setting the film in place, reducing tension, or preventing post-application separation. 
     
     
         32 . The method of  claim 29 , wherein the at least one location on the substrate is near a middle of the substrate.