Wire rod and steel wire for springs having excellent corrosion fatigue resistance properties, and method for producing same

Abstract

A wire rod and a steel wire which are for springs and have excellent corrosion fatigue resistance properties, and a method for producing same. The wire rod and steel wire containing, in wt ¾, 0.40-0.70% of C, 1.20-2.30% of Si, 0.20-0.80% of Mn, 0.20-0.80% of Cr, 0.015% or less of P, 0.015% or less of S, and 0.010% or less of N, with the remainder including Fe and other unavoidable impurities, along with at least one among 0.01-0.20% of V and 0.01-0.10% of Nb, wherein the V and Nb satisfy relational expression 1 below, the average grain size of prior austenite is no greater than 20 μm, and the surface decarburization depth is no greater than 0.1 mm. [V]+[Nb]□0.08 (where the V and Nb contents are in wt ¾).  [Relational expression 1]

1 . A wire rod for a spring, the wire rod containing: by wt %, C: 0.40 to 0.70%, Si: 1.20 to 2.30%, Mn: 0.20 to 0.80%, Cr: 0.20 to 0.80%, P: 0.015% or less, S: 0.015% or less, N: 0.010% or less, one or two of V: 0.01 to 0.20% and Nb: 0.01 to 0.10%, and a balance of Fe and other unavoidable impurities,
 wherein Relational Expression 1: [V]+[Nb]≥0.08 is satisfied, wherein, [V] and [Nb] represent the content of V and Nb in wt %,   wherein a microstructure of the wire rod is a composite structure of ferrite and pearlite,   a ratio of an amount of non-diffusible hydrogen to an amount of diffusible hydrogen is 2.67 or more,   an average grain size of prior austenite is 20 μm or less, and   the wire rod includes 3.17×10 4 /mm 2  or more of carbides containing 50 wt % or more of one or two of V and Nb.   
     
     
         2 . The wire rod of  claim 1 , further containing by wt %, one or two of Ti: 0.01 to 0.15% and Mo: 0.01 to 0.40%. 
     
     
         3 . The wire rod of  claim 1 , further containing by wt %, one or two of Cu: 0.01 to 0.40% and Ni: 0.10 to 0.60%. 
     
     
         4 . The wire rod of  claim 1 , wherein the wire rod contains, by wt %, Si: 1.20 to 1.49%. 
     
     
         5 . The wire rod of  claim 1 , wherein a fraction of the ferrite is 5 to 35 area %. 
     
     
         6 . The wire rod of  claim 1 , wherein a depth of surface decarburization is 0.1 mm or less. 
     
     
         7 . A steel wire for a spring, the steel wire containing: by wt %, C: 0.40 to 0.70%, Si: 1.20 to 2.30%, Mn: 0.20 to 0.80%, Cr: 0.20 to 0.80%, P: 0.015% or less, S: 0.015% or less, N: 0.010% or less, one or two of V: 0.01 to 0.20% and Nb: 0.01 to 0.10%, and a balance of Fe and other unavoidable impurities,
 wherein Relational Expression 1: [V]+[Nb]≥0.08 is satisfied, wherein [V] and [Nb] represent the content of V and Nb in wt %,   a ratio of an amount of non-diffusible hydrogen to an amount of diffusible hydrogen is 2.67 or more,   an average grain size of prior austenite is 20 μm or less, and   the steel wire includes 3.17×10 4 /mm 2  or more of carbides containing 50 wt % or more of one or two of V and Nb.   
     
     
         8 . The steel wire of  claim 7 , further containing by wt %, one or two of Ti: 0.01 to 0.15% and Mo: 0.01 to 0.40%. 
     
     
         9 . The steel wire of  claim 7 , further containing by wt %, one or two of Cu: 0.01 to 0.40% and Ni: 0.10 to 0.60%. 
     
     
         10 . The steel wire of  claim 7 , wherein a depth of surface decarburization is 0.1 mm or less. 
     
     
         11 . The steel wire of  claim 7 , wherein a microstructure of the steel wire is, in an area fraction, 10% or less of residual austenite and remaining tempered martensite.