Method for preparing moulded polyureapolyurethane flexible foams

Abstract

A method to prepare polyurethane and/or polyurea flexible foams which comprises reacting: A. an organic polyisocyanate composition B. an isocyanate-reactive composition containing: a. at least one high Mw isocyanate-reactive compound b 1 . a primary or secondary amino-functional compound (so-called chain-extender) of Mw below 1000 in an amount of less than 1% by wt of high Mw isocyanate-reactive compound(s) or b 2 . a mixture of at least two chain extenders of which at least one is a primary or secondary amino-functional compound of Mw below 1000, in an amount of 0.1% to 10% by wt of high Mw isocyanate-reactive compound(s) C. H 2 O D. optionally catalysts E. optionally further blowing agents which are different from H 2 O. F. optionally further conventional additives.

We claim: 
     
       1. A method to prepare polyurethane and/or polyurea flexible foams which comprises reacting: A. an organic polyisocyanate composition   B. an isocyanate-reactive composition containing: a. at least one high Mw isocyanate-reactive compound   b 1 . a compound selected from the group consisting of DETDA and isophorone diamine of Mw below 1000 in an amount of less than 1% by wt of high Mw isocyanate-reactive compound(s) or     b 2 . a mixture of at least two chain extenders of which at least one is a compound selected from the group consisting of DETDA and isophorone diamine of Mw below 1,000, in an amount of 0.1% to 10% by wt of which Mw isocyanate-reactive compound(s)   C. H 2  O   D. optionally catalysts   E. optionally further blowing agents which are different from H 2  O.   
     
     
       F. optionally further conventional additives. 
     
     
       2. A method according to claim 1 in which the primary or secondary amino-functional compound in the mixture b 2  is present in an amount of less than 1% by weight of high Mw isocyanate-reactive compound(s). 
     
     
       3. A method according to any one of claims 1 or 2, wherein the high molecular weight isocyanate-reactive compound(s) has/have a molecular weight of 1000 to 10,000, and a functionality of 2-4, and are selected from the group consisting of polyoxyalkylene polyether polyols and polyoxyalkylene polyether polyamines. 
     
     
       4. A method according to .[.any one of the preceding claims.]. .Iadd.claim 3 .Iaddend.wherein the mixture of chain-extenders b 2  comprises a second chain-extender selected among amino-compounds, amino-alcohols, polyols. 
     
     
       5. A method according to .[.any one of the preceding claims.]. .Iadd.claim 4 .Iaddend.wherein there is used H 2  O in an amount of 1.5% to 10% by wt of high Mw isocyanate-reactive compound(s). 
     
     
       6. A method according to claim 5 wherein there is used H 2  O in an amount of 2.5% to 6% by weight of high Mw isocyanate-reactive compound(s). 
     
     
       7. A method according to .[.any one of the preceding claims.]. .Iadd.claim 6 .Iaddend.wherein the isocyanate composition (A), the isocyanate-reactive composition (B) and H 2  O are used in such amounts to provide an isocyanate index ranging from 40 to 120. 
     
     
       8. A method according to claim 7 wherein there is provided an isocyanate index ranging from 50 to 100. 
     
     
       9. A reaction system for performing a method according to any one of the preceding claims which comprises; A. an organic polyisocyanate composition   B. an isocyanate-reactive composition containing; a. at least one high Mw isocyanate-reactive compound   b 1 . an amino-functional compound (so-called chain-extender) of Mw below 1000 a primary or secondary in an amount of less than 1% by wt of high Mw isocyanate-reactive compound(s) or   b 2 . a mixture of at least two chain extenders of which at least one is an amino-functional compound of Mw below 1000, in an amount of 0.1% to 10% by wt of high Mw isocyanate-reactive compound(s)     C. H 2  O   D. optionally catalysts   E. optionally further blowing agents which are different from H 2  O   F. optionally further conventional additives.   
     
     
       10. A flexible foam which is obtained by using a method according to .[.any one of claims 1 to 8.]. .Iadd.claim 1 .Iaddend.or which is obtained by using a reaction system according to claim 9.