Glass microspheres for use in films and projection screen displays and methods

Abstract

Glass microspheres and rear projection screens containing glass microspheres, which combine a desirable index of refraction (preferably, no greater than about 1.70) and low levels of defects (e.g., bubbles, visible haziness, frostiness, or opacity, substantially nonspherical shapes) upon formation are provided. Also provided is a coating method of placing microspheres on a film for use in a rear projection screen.

What is claimed is:  
     
       1. A projection screen comprising a plurality of glass microspheres in optical contact with a substrate and embedded in an opaque matrix; 
       wherein the glass microspheres: 
       having an index of refraction of no greater than about 1.70;  
       comprise, on a theoretical oxide basis based on the amount of starting materials;  
       greater than about 5 wt-% of an alkali metal oxide selected from the group consisting of Na 2 O, K 2 O, Li 2 O, and mixtures thereof;  
       no greater than about 40 wt-% SiO 2 ; and  
       no less than about 10 wt-% TiO 2 ; and  
       as produced have less than about 15% defects in a population.  
     
     
       2. The projection screen of  claim 1  wherein the glass microspheres comprise, on a theoretical oxide basis based on starting materials; 
       no greater than about 40 wt-% SiO 2 ;  
       no less than about 10 wt-% TiO 2 ;  
       no less than about 5 wt-% B 2 O 3 ;  
       no less than about 20 wt-% of an alkaline earth modifier selected from the group consisting of BaO, SrO, and mixtures thereof; and  
       greater than about 5 wt-% of an alkali metal oxide selected from the group consisting of Na 2 O, K 2 O, Li 2 O, and mixtures thereof.  
     
     
       3. The projection screen of  claim 1  wherein the glass microspheres comprise, on a theoretical oxide basis based on starting materials: 
       no greater than about 31 wt-% SiO 2 ;  
       no less than about 15 wt-% TiO 2 ;  
       no less than about 10 wt-% B 2 O 3 ;  
       no less than about 25 wt-% of an alkaline earth modifier selected from the group consisting of BaO, SrO, and mixtures thereof; and  
       no less than about 10 wt-% of an alkali metal oxide selected from the group consisting of Na 2 O, K 2 O, Li 2 O, and mixtures thereof.  
     
     
       4. The projection screen of  claim 1 , wherein the microspheres have an index of refraction of about 1.50 to about 1.70. 
     
     
       5. The projection screen of  claim 1  wherein the microspheres comprise Li 2 O. 
     
     
       6. The projection screen of  claim 5  wherein the microspheres comprise, on a theoretical oxide basis based on starting materials, at least about 0.25 wt-% Li 2 O. 
     
     
       7. The projection screen of  claim 1  wherein the microspheres are prepared from a composition that melts below a temperature of about 1350° C. 
     
     
       8. The projection screen of  claim 1  wherein the microspheres are coated with a flow control agent. 
     
     
       9. A projection screen comprising a plurality of glass microspheres in optical contact with a substrate and embedded in an opaque matrix; wherein the glass microspheres: 
       have an index of refraction of no greater than about 1.70;  
       comprise, on a theoretical oxide basis based on the amount of starting materials;  
       no greater than about 40 wt-% SiO 2 ;  
       no less than about 10 wt-% TiO 2 ;  
       no less than about 5 wt-% B 2 O 3 ;  
       no less than about 20 wt-% of an alkaline earth modifier selected from the group consisting of BaO, SrO, and mixtures thereof; and  
       greater than about 5 wt-% of an alkali metal oxide selected from the group consisting of Na 2 O, K 2 O, Li 2 O, and mixtures thereof.  
     
     
       10. A film comprising a plurality of glass microspheres disposed on a substrate and embedded in an opaque matrix; 
       wherein the glass microspheres: 
       have an index of refraction of no greater than about 1.70;  
       comprise, on a theoretical oxide basis based on the amount of starting materials;  
       greater than about 5 wt-% of an alkali metal oxide selected from the group consisting of Na 2 O, K 2 O, Li 2 O, and mixtures thereof, with the proviso that Li 2 O is present;  
       no greater than about 40 wt-% SiO 2 ; and  
       no less than about 10 wt-% TiO 2 ; and  
       as produced have less than about 15% defects in a population.  
     
     
       11. A glass microsphere comprising, on a theoretical oxide basis, based on starting materials: 
       no greater than about 40 wt-% SiO 2 ;  
       no less than about 10 wt-% TiO 2 ;  
       no less than about 5 wt-% B 2 O 3 ;  
       no less than about 20 wt-% of an alkaline earth modifier selected from the group containing of BaO, SrO, and mixtures thereof; and  
       greater than about 5 wt-% of an alkali metal oxide selected from the group containing of Na 2 O, K 2 O, Li 2 O, and mixtures thereof, with the proviso that Li 2  O is present.  
     
     
       12. The glass microsphere of  claim 11  comprising: 
       no greater than about 31 wt-% SiO 2 ;  
       no less than about 15 wt-% TiO 2 ,  
       no less than about 10 wt-% B 2 O 3 ;  
       no less than about 25 wt-% of an alkaline earth modifier selected from the group containing of BaO, SrO, and mixtures thereof; and  
       no less than about 10 wt-% of an alkali metal oxide selected from the group containing of Na 2 O, K 2 O, Li 2 O, and mixtures thereof.  
     
     
       13. The microsphere of  claim 11  which has a diameter of less than about 150 micrometers. 
     
     
       14. The glass microsphere of  claim 11  which has an index of refraction of about 1.50 to about 1.70. 
     
     
       15. The glass microsphere of  claim 11  comprising, on a theoretical oxide basis based on starting materials, at least about 0.25 wt-% Li 2 O. 
     
     
       16. The glass microsphere of  claim 11  which is prepared from a composition that melts below a temperature of about 1350° C. 
     
     
       17. The glass microsphere of  claim 11  further comprising a coating comprising a flow control agent. 
     
     
       18. A noncalcium-containing glass microsphere comprising, on a theoretical oxide basis, based on starting materials: 
       no greater than about 40 wt-% SiO 2 ;  
       no less than about 10 wt-% TiO 2 ;  
       no less than about 5 wt-% B 2 O 3 ;  
       no less than about 20 wt-% of an alkaline earth modifier selected from the group containing of BaO, SrO, and mixtures thereof; and  
       greater than about 5 wt-% of an alkali metal oxide selected from the group containing of Na 2 O, K 2 O, Li 2 O, and mixtures thereof.  
     
     
       19. A method of making a film for use in a projection screen, the method comprising: 
       providing a substrate having an opaque matrix disposed thereon; and  
       applying glass microspheres from a rolling bank of microspheres onto the opaque matrix under conditions effective to produce microspheres in optical contact with the substrate and embedded in the opaque matrix.  
     
     
       20. The method of  claim 19  wherein applying glass microspheres from a rolling bank comprises: 
       contacting the opaque matrix on the substrate with sufficient glass microspheres to form multiple layers of glass microspheres between the substrate and a pack roll;  
       pressing the glass microspheres into the opaque matrix on the substrate to form a monolayer of embedded microspheres, wherein the apex of a majority of the microspheres are in direct contact with the substrate underlying the opaque matrix.